中文摘要：

摘要：采用粉末冶金法制备了Fe-12Cr-2．5W-0．4Ti-0．3Y203合金，研究了压制压力及烧结温度对烧结体组织与性能的影响。结果表明：铬、钨原子在高能球磨过程中未能完全固溶于α-Fe中，而在烧结过程中能实现完全固溶；压坯密度和抗弯强度随压制压力增大而增加，并在压力达到700MPa后趋于稳定；提高压制压力与烧结温度可提高烧结体抗拉强度，在压制压力700MPa，烧结温度1400℃的条件下，烧结体抗拉强度为416．7MPa，材料断裂方式为韧性断裂。

英文摘要：

The Fe-12Cr-2. 5W-0. 4Ti-0. 3Y2O3 alloy was prepared by powder metallurgy method, and the effects of pressing pressure and sintering temperature on microstructure and properties of the sintered body were studied. The results show that chromium and tungsten atoms had not completely entered into α-Fe in solid solution mode during milling, but complete solid solution could be carried out during sintering. The pressed compact density and bending strength raised with the increase of the pressing pressure and gradually tended to stability after the pressure was up to 700 MPa. The increase of pressing pressure and sintering temperature was advantageous to the raising of the sintered body strength. The sintered body tensile strength was 416. 7 MPa when pressing pressure was 700 MPa and sintering temperature was 1 400 ℃, and the fracture mode was ductile fracture.