中文摘要：

利用乙二胺活化纤维素,将活化后的纤维素（Ce）和热塑性聚氨酯（TPU）分别溶于氯化锂（LiCl）-N,N-二甲基乙酰胺（DMAC）体系,制得纤维素-热塑性聚氨酯（Ce-TPU）共混膜。利用傅里叶红外光谱仪（FT-IR）、扫描电子显微镜（SEM）、X射线衍射仪（XRD）、单纤强力仪、折痕恢复性测定仪对共混膜的结构和性能进行表征。结果表明：Ce和TPU相容性良好,w（TPU）=30%时为共混膜的最优配比,此时断裂强力较纯纤维素膜略有提高,断裂伸长率提高了68%,折皱回复角提高了17%,共混膜的抗皱性和弹性有所改善。

英文摘要：

The cellulose （Ce） was activated by ethylenediamine, and the blend films （Ce-TPU） were prepared by using the activated cellulose as material, solution casting lithium chloride（LiCl）-N,N-dimethylacetamide（DMAC） as solvent system and thermoplastic polyurethane（TPU） as finish agent. Structure and properties of the blend films were investigated by Fourier Infrared spectroscopic analysis （FT-IR）, X-Ray Diffraction （XRD）, tensile strength test and crease recovery test, respectively. Results demonstrated that the compatibility of cellulose and TPU was good. The optimization ratio of blend films was 30 % of TPU mass fraction. For the optimal blend films, the breaking force was slightly enhanced, while the elongation at break was improved by 68%, and the crease recovery angle increased by 17%, the wrinkle resistance and elasticity were better than those of pure cellulose films.