中文摘要：
采用传统降温法生长了一系列的K（H1-xD）2PO4晶体。粉末X射线衍射（XRD）证明氘化后晶体的对称性并没有发生改变，晶胞参数α随氘含量的增加而增大，参数c则小幅度增大。对晶体的高分辨X射线衍射研究，结果表明KDP—DKDP混晶中，D取代部分的H原子对晶体的结晶完整性影响较小。
英文摘要：
A serials of K（H1-xDx）2PO4 crystals were grown by using traditional method from deuterated solu- tions. From the results of powder X-ray diffraction （XRD）, it shows that the no changes occurred on symmetry of structure in K（H1- xDx ）2PO4 crystals, while lattice parameter a increases with a increase of deuterium con- tent of crystal. High resolution XRD was taken to characterize crystalline perfection. It was indicated that crys- talline perfection was destroyed slightly by the replacement of partial H atoms by D atoms in KDP-DKDP mixed crystals.
同期刊论文项目
同项目期刊论文
Appearance of [110] Orientated Growth Layer on (100) Face and Exposure of(111) Faces of Cubic Bismut
Improvement of growth habit and optical properties of rapidly grown KDP crystal by adding diethylene
Atomic Force Microscopic Investigation on Surface Structure Related to Growth Kinetics on (101) Face
期刊信息
位置：