分析了定向凝固Ti-43Al-3Si（原子分数,%）合金在3—90μm/s的生长速度下的稳态生长区组织.在定向凝固过程中经历下列反应：L→Ti5Si3,L→α＋Ti5Si3,α→α2（Ti3Al）＋γ（TiA1）,α2→γ＋Ti5Si3,其中,α与Ti5Si3共晶是合金最显著的凝固行为.当生长速度大于20μm/s时,还出现L→γ＋Ti5Si3.随着生长速度增大,稳态组织逐渐由粗胞晶向细胞晶、胞状枝晶及枝晶转变,起稳定α相作用的Ti5Si3相由低速时分布于α相中逐渐向高速时分布于凝固γ相中转变,不利于该合金的引晶.选择10μm/s的初始生长速度,既能减少到达稳态生长的距离,又能保证引晶效果.
英文摘要：
Microstructure evolutions in the steady-state growth region of directionally solidified Ti-43Al-3Si （atomic fraction, %） alloy were studied at growth rates of 3-100 μm/s. There are four main phase transitions during directional solidification： L→TisSi3, L→α＋Ti5Si3, α→α2（Ti3Al）＋γ（TiAl） and α2→γ＋Ti5Si3, especially, the eutectic reaction of α and Ti5Si3 is the typical solidification behavior. When the growth rate exceeds 20 μm/s, another phase transition of L→γ＋Ti5Si3 also happens. With increase of growth rate, the steady-state growth microstructure changes from coarse cells to fine cells, to cellular dendrites and then to dendrites. The TisSia phase stabilizing α phase distributes in the α matrix at a low growth rate, and in the solidified γmatrix at a relatively high growth rate, which is unfavorable in seeding. When the growth rate is 10 μm/s, the distance needed to reach steady-state region becomes shorter, which is favourable in seeding for the present alloy.
同期刊论文项目
同项目期刊论文
Phase-field simulation of lamellar growth for a binary eutectic alloy. LI Xin-zhong(李新中)1, 2, LIU Do
Dependency of microhardness on solidification processing parameters and microstructure characteristi
Influence ofthermalstabilizationonthesoluteconcentrationofthemeltin directional solidification. Dong
Effect of growth rate on microstructure parameters and microhardness in directionally solidified Ti&
Improvement of microstructure and mechanical properties adding Mg3Zn6Y icosahedral phase alloy. Huij
Dependency of microstructure parameters and microhardness on the temperature gradient for directiona
Microstructure evolution in directionally solidified Tie(50, 52) at%Al alloys. Dongmei Liu, Xinzhong
Numerical computations for temperature, fraction of solid phase and composition couplings in ternary
An analysisofnon-equilibriumperitecticreactiondrivenbysolutediffusion under atemperaturegradient Don
Jianglei Fan, Xinzhong Li, Yanqing Su, Jingjie Guo, Hengzhi Fu. Dependency of microhardness on solid
Yanqing Su, Dongmei Liu, Xinzhong Li, Liangshu Luo, Jingjie Guo, HengzhiFu. Preparation of theinitia
Jianglei Fan, Xinzhong Li, Yanqing Su,Jingjie Guo, Hengzhi Fu.The microstructure parameters and micr
Li Xin-zhong, Liu Dong-mei, Su Yan-qing, Guo Jin-gjie, Fu Heng-zhi. Phase-field simulation of lamell
Su Yanqing, Liu Dongmei, Li Xinzhong, Luo Liangshun, Guo Jingjie, Fu Hengzhi. Microstructure evoluti
期刊信息
位置：