采用液相沉积法在不同pH值溶液中制备了多孔氢氧化镍（Ni（OH）2）薄膜.当溶液pH值在7.5～8.8之间变化时,能在基片上形成均匀连续的由Ni（OH）2纳米棒搭接组成的多孔薄膜,主要晶型为β-Ni（OH）2.溶液pH值的微小变化会引起薄膜中棒状Ni（OH）2尺寸的显著改变;当pH=7.5时,Ni（OH）2纳米棒的长度约为80nm,直径约为50nm;当pH=7.8时,Ni（OH）2纳米棒的长度增大到180nm,直径约为60nm;当pH=8.0时,Ni（OH）2纳米棒的长度显著增大约为300nm,直径约为70nm.然而,当pH=8.3时,Ni（OH）2纳米棒的长度减小约为230nm,直径约为80nm;当pH=8.8时,纳米棒长度迅速减小约为110nm,直径减小约为55nm.结合Ni（OH）2成核、生长过程和β-Ni（OH）2晶体结构特点讨论了溶液pH值对Ni（OH）2薄膜微观形态的影响机制.
英文摘要：
Nickel hydroxide （Ni（OH）2） thin films were deposited from a variety of solutions with different pH values by liquid phase deposition. Continuous Ni（OH）2 thin films were obtained within the pH ranging from 7.5 to 8.8. The nucleation and growth process of Ni（OH）2, and β-Ni（OH）2 crystallization were used to discuss the influence of solution pH on the microstructures of the Ni（OH）2 films. The thin films are made of Ni（OH）2 nanorods mainly with β-Ni（OH）2 crystallinity and there are a lot of open pores between the nanorods in the Ni（OH）2 films. The dimensions of Ni（OH）2 nanorods change remarkably with the pH of reactive solutions. When solution＇s pH is 7.5, the length of nanorods is about 80nm and the diameter is about 50nm. When solution＇s pH increases to 7.8, the length of nanorods increases to about 180nm and the diameter is about 60nm. When solution＇s pH increases to 8.0, the length of nanorods sharply increases to about 300nm and the diameter is about 70nm. However, when solution＇s pH increases to 8.3, the length of nanorods decreases to about 230nm and the diameter is about 80nm. When solution＇s pH increases to 8.8, the length of nanorods sharply decreases to about 110nm and the diameter is about 55nm.
同期刊论文项目
同项目期刊论文
Characterization and normalization factors of abiotic resource depletion for life cycle impact asses
Influence of Different Surfatants on Morphology of Single Crystal Ce2O(CO3)2·H2O and Formation Mecha
FEA modeling of effect of axial feeding velocity on strain field of rotary swaging process of pure m
Measurement of microemulsion zone and preparation of monodispersed cerium oxide nanoparticles by W/O
Facile synthesis of hydrophobic microporous silica membranes and their resistance to humid atmospher
Preparation and characterization of nanostructured Ni(OH)(2) and NiO thin films by a simple solution
Catalytically active gold nanoparticles confined in periodic mesoporous organosilica (PMOs) by a mod
3D finite element modeling of cogging-down rotary swaging of pure magnesium square billet - Revealin
Functionalization of periodic mesoporous organosilica with ureidopropyl groups by a direct synthesis
期刊信息
位置：