中文摘要：
以三氯甲烷为溶剂,氨丙基三甲氧基硅烷（APTMS）为修饰剂通过后接枝法对周期性介孔氧化硅材料（PMOs）进行修饰.通过固态NMR、氮气吸附、元素分析和UV-vis吸光度测试等手段来表征材料.结果表明,氨丙基基团通过共价连接的方式成功修饰到PMOs材料.尽管随着APTMS修饰量的增加,比表面积、孔容和孔径都呈下降趋势,但经25%APTMS修饰的PMOs材料依然具有良好的介孔结构,其表面积为604m^2·g^-1,孔容为0.62cm^3·g^-1,孔径狭窄分布在4.5～5.0nm之间.修饰后的PMOs对氯金酸有明显的吸附作用.
英文摘要：
Aminopropyl groups were used to functionalize the pore channels of periodic mesoporous organosilicas（PMOs） by the post-grafting method. The final materials were investigated by means of XRD, TEM, solid-state NMR, N2 adsorption and Elementar Analysis. The results show that bridging groups in the framework do not cleave and amino groups are attached covalently to the pore wall of periodic mesoporous organosilica after functionalization. The mesoscopic order remains good with increasing aminopropyl groups coverage up to 25mol%. The surface area, pore volume and pore size tend to decrease as the concentration of APTMS increases, but the materials with 25mol% aminopropyl groups still preserve a desirable pore structure, with surface area of 604m^2·g^-1, pore volume of 0.62cm^3·g^-1 and sharp pore size distribution centered between 4.5nm and 5nm. Aminopropyl-functionalized PMOs facilitates absorption of （HAuCl）-complex.
同期刊论文项目
同项目期刊论文
Characterization and normalization factors of abiotic resource depletion for life cycle impact asses
Influence of Different Surfatants on Morphology of Single Crystal Ce2O(CO3)2·H2O and Formation Mecha
FEA modeling of effect of axial feeding velocity on strain field of rotary swaging process of pure m
Measurement of microemulsion zone and preparation of monodispersed cerium oxide nanoparticles by W/O
Facile synthesis of hydrophobic microporous silica membranes and their resistance to humid atmospher
Preparation and characterization of nanostructured Ni(OH)(2) and NiO thin films by a simple solution
Catalytically active gold nanoparticles confined in periodic mesoporous organosilica (PMOs) by a mod
3D finite element modeling of cogging-down rotary swaging of pure magnesium square billet - Revealin
Functionalization of periodic mesoporous organosilica with ureidopropyl groups by a direct synthesis
Preparation and characterization of vinyl-functionalized mesoporous SBA-15 silica by a direct synthe
Catalytically active gold nanoparticles confined in periodic mesoporous organosilica(PMOs) by a modi
期刊信息
位置：