中文摘要：
采用N2-吸附脱附、XRD、Raman光谱和TEM等表征技术研究了柠檬酸溶胶-凝胶法制备的Ce1-xMnxO2（0≤x≤1）样品的织构及晶相结构.结果表明,Ce1-xMnxO2样品的N2吸附等温线为Ⅳ型,滞后环为H1型,最可几孔径处在2.5～3.7 nm范围.由XRD测得的样品晶粒大小与由TEM测定的颗粒尺寸相近,表明制备的样品具有较好的分散性,但是样品的组成对颗粒大小有明显的影响,Mn浓度适中样品（x=0.3～0.7）的颗粒（1～5 nm）明显小于低Mn浓度样品（x＜0.3）和高Mn浓度样品（x＞0.7）的颗粒（10～50 nm）.尽管在x＞0.7时,XRD未能检测到样品中有α-Mn2O3晶粒存在,但Raman光谱结果表明,所有Ce1-xMnxO2混合氧化物均以α-Mn2O3相和立方CeO2相CeMn-O固溶体形式存在.
英文摘要：
Textural and structure characterizations of Ce1-xMnxO1 （0≤x≤1） samples were studied by N2 adsorption/ desorption, XRD and Raman spectroscopy. The N2 adsorption/desorption isotherms are found to be Ⅳ-type according to BDDT and their related hysteresis loops are H1 type. Pore size distribution of the Ce1-xMnxO2 samples is in the mesopores range with Rp （max） between 2.5 nm and 3.7 nm. Particle sizes of the samples with both high Mn （x〉0.7） and low Mn （x〈0.3） contents are larger than those with 0.3≤x≤0.7. Raman spectroscopic results show that the Ce1-xMnxO2 （x ≠0, 1） samples contain mixed phases of α-Mn2O3 and Ce-Mn-O solid solution, although the presence of α-Mn2O3 phase is not detected in the XRD measurement of the samples with x≤0.7, suggesting that Raman spectroscopy is more sensitive in the structural characterization of Ce1-xMnxO2 samples.
同期刊论文项目
同项目期刊论文
Sulfur-tolerant Pt/Gd2O3-CeO2-Al2O3 catalyst for high efficiency H2 production from autothermal refo
The influence of preparative parameters on the adhesion of alumina washcoats deposited onmetallic su
Biodesulfurization of DBT in tetradecane and crude oil by a facultative thermophilic bacterium Mycob
Effect of thermal on structure and catalytic activity of supported Fischer-Tropsch nano-cobalt catal
High-performance HTLcs-derived CuZnAl catalysts for hydrogen production via methanol steam reforming
Cometabolic degradation of dibenzofuran and dibenzothiophene by a newly isolated carbazole degrading
Base-free Catalytic Aerobic Oxidation of Mercaptans for Gasoline Sweetening over HTLcs-derived CuZnA
Paper-like microfibrous nickel catalyst for hydrogen production via ammonia decomposition in fuel ce
Effect of air-exposure on reduction behavior of a Fe-Mn-Cu-K/SiO2 Fischer-Tropsch synthesis catalyst
Thin-sheet Ag/Ni-fiber catalyst for gas-phase selective oxidation of benzyl alcohol with molecular o
Effects of Impregnation Sequence on the Microstructure and Performances of Cu-Co based Catalysts for
Co-decorated carbon nanotubes as a promoter of Co-Mo-K oxide catalyst for synthesis of higher alcoho
Simultaneous biodetoxification of S, N and O pollutants by engineering a carbazole degrading gene ca
Selective biodegradation of S and N heterocycles by a recombinant Rhodococcus erythropolis strain co
Paper-like 3-Dimensional carbon nanotubes (CNTs)-microfiber hybrid: A promising macroscopic structur
Miniature NH3 Cracker Based on Microfibrous Entrapped Ni-CeO2/Al2O3 Catalyst Monolith for Portable F
Effects of potassium on MgO-supported Fe-Mn catalysts for the hydrogenation of carbon monoxide to li
Effect of manganese on an iron-based Fischer-Tropsch synthesis catalyst prepared from ferrous sulfat
Sustainable Production of Acrolein: Investigation of Solid Acid-Base Catalysts for Gas-phase Dehydra
Comparative study of atmospheric and high pressure CO2 reforming of methane over Ni/MgO-AN catalyst,
Cataluminescence and catalytic reactions of ethanol oxidation over nanosized Ce1-xZrxO2 (0( x (1) ca
Thiophene Adsorption and Activation on MoP(001), (-Mo2N(100), and Ni2P(001): Density Functional Theo
Deep desulfurization of diesel oil and crude oils by a newly isolated Rhodococcus erythropolis strai
“Green” route to 6 hydroxy 3 succinoyl pyridine from (S) nicotine of tobacco waste by whole cells of
A large pore-size mesoporous zirconia supported cobalt catalyst with good performance in Fischer-Tro
Influences of preparation methods of ZrO2 support and treatment conditions of Cu/ZrO2 catalysts on s
Effect of reduction temperature on a spray-dried iron-based catalyst for slurry Fischer-Tropsch synt
Highly sulfur-tolerant Pt/Ce0.8Gd0.2O1.9 catalyst for steam reforming of liquid hydrocarbons in fuel
Carbon nanotube-promoted Co-Cu catalyst for highly efficient synthesis of higher alcohols from synga
Effect of reduction temperature and duration on iron-based catalysts for slurry phase Fischer-Tropsc
Preparation and characterization of carbon nanotube-promoted Co–Cu catalyst for higher alcohol synth
Deuterium tracer study of pressure effect on the product distribution for the cobalt-catalyzed Fisch
Effect of reaction conditions on the catalytic performance of Fe-Mn catalyst for Fischer-Tropsch syn
Sustainable Production of Acrolein: Gas-phase Dehydration of Glycerol over 12-tungstophosphoric Acid
HTLcs-derived CuZnAl oxide catalysts for aerobic oxidative removal of gasoline-range organo-sulfur c
Study on the iron-silica interaction of a co-precipitated Fe/SiO2 Fischer-Tropsch synthesis catalyst
Monolithic microfibrous nickel catalyst co-modified with ceria and alumina for miniature hydrogen pr
In situ diffuse reflectance FTIR study of CO adsorbed on cobalt catalyst supported by silica with di
期刊信息
位置：