中文摘要：
采用硅烷偶联剂对生物活性玻璃（BG）进行表面修饰以改善其与高分子的亲和性。通过溶胶凝胶法制得BG,将氨丙基三乙氧基硅烷（APTES）键连到BG表面,采用FTIR、TG、激光粒度仪等对修饰前后的BG进行表征,并通过细胞实验对材料的细胞相容性进行初步研究。结果表明,修饰后BG的FTIR图谱上出现归属于C—H的伸缩振动吸收峰,在DTG曲线上观察到明显的有机基团燃烧失重峰,表明APTES接枝到生物玻璃表面;而MC-3T3细胞增殖测定和SEM结果显示经表面修饰后的BG更有利于细胞的生长增殖。
英文摘要：
The silane coupling agent was used to modify the inorganic bioactive glass（BG） surface aiming at improving affinity with polymer.BG was prepared by sol-gel method,then 3-aminopropyltriethoxysilane（APTES） was grafted onto BG surface.FTIR,TG and laser particle size analyzer were adopted to characterize BG before and after modification,and the cell biocompatibility of the material was studied preliminarily through cell culture.The results show that stretching vibration attributed to saturated C—H appears in FTIR spectrum of modified BG,and remarkable mass loss resulted from combustion of organic group is observed in DTG curve,which suggest that APTES has been bonded onto BG surface.The MC-3T3 cell proliferation measurement and SEM photos show that the modified BG is in favor of the cell growth and proliferation compared with unmodified BG.
同期刊论文项目
同项目期刊论文
Mineralization regulation and biological influence of bioactive glass-collagen-phosphatidylserine co
Poly(lactide-co-glycolide)/titania Composite Microsphere-Sintered Scaffolds for Bone Tissue Engineer
Modified PHBV scaffolds by in situ UV polymerization: Structural characteristic, mechanical properti
Surface Modification of PHBV Films with Different Functional Groups: Thermal Properties and In Vitro
In vivo and in vitro osteogenesis of stem cells induced by controlled release of drugs from microsph
Genipin-cross-linked collagen/chitosan biomimetic scaffolds for articular cartilage tissue engineeri
Microsphere-based drug releasing scaffolds for inducing osteogenesis of human mesenchymal stem cells
Redifferentiation of Dedifferentiated Chondrocytes by Adenoviral Vector-Mediated TGF-beta 3 and Coll
In Situ Fabrication of Nano-hydroxyapatite in a Macroporous Chitosan Scaffold for Tissue Engineering
Characterization and biocompatibility of nanohybrid scaffold prepared via in situ crystallization of
Preparation of Regular Micropitted Polylactide Films via Phase Separation and Their Cell Affinity Ev
A novel hydrophilic poly(lactide-co-glycolide)/lecithin hybrid microspheres sintered scaffold for bo
A protein/antibiotic releasing poly(lactic-co-glycolic acid)/lecithin scaffold for bone repair appli
Synthesis and Characterization of New Unsaturated Degradable Poly(ether ester amide)s Containing Eth
Biomimetic Synthesis of Porous Composite Scaffold Composed of Nano-Hydroxyapatite and Chitosan by Fr
In-vitro osteogenesis of synovium stem cells induced by controlled release of bisphosphate additives
Progress in the Biomineralization Study of Bone and Enamel and Biomimetic Synthesis of Calcium Phosp
Enhancing Alendronate Release from a Novel PLGA/Hydroxyapatite Microspheric System for Bone Repairin
Surface characterization of polyethylene terephthalate films treated by ammonia low-temperature plas
Structure and surface nanomechanics of poly(L-lactide) from thermally induced phase separation proce
Layer-by-layer assembly of type I collagen and chondroitin sulfate on aminolyzed PU for potential ca
Preparation and evaluation of biomimetric nano-hydroxyapatite-based composite scaffolds for bone-tis
期刊信息
位置：