中文摘要：
在氩气气氛下,采用扩散偶法研究了1323-1473 K下的Fe2O3-TiO2体系的固相反应.使用电子探针对扩散偶的微观形貌进行观察,并对Fe、Ti离子的扩散摩尔分数曲线进行定量分析.动力学分析表明,氩气下体系的固相反应受铁、钛和氧离子的扩散控制.用Boltzmann-Matano法计算了体系的互扩散系数,其数量级在10-13-10-10 cm2·s-1范围内,并随着温度和Ti离子摩尔分数的增大而升高.氩气气氛下体系的扩散活化能约为356.06 kJ·mol-1,远比空气下的大,表明外界气氛中氧分压对体系的反应机理有重要影响.
英文摘要：
ABSTRACT The diffusion couple method was used to study the solid-state reaction of the Fe2 O3-TiO2 system in the temperature range of 1323 K to 1473 K in argon. The microstructure of the diffusion couple and the diffusion concentration profiles of Fe and Ti were determined by electron probe microanalysis （ EPMA） . According to kinetic analysis, this solid-state reaction is controlled by the diffu-sion of Fe, Ti and O ions. The inter-diffusion coefficient, which increases with the increasing temperature and concentration of Ti ions, was calculated by the Boltzmann-Matano method, and its order of magnitude is in the range of 10 -13 to 10 -10 cm2·s-1 . The diffusion activation energy （ about 356.06 kJ·mol-1 ） of the system in argon is much bigger than that in air, which indicates that the partial pres-sure of oxygen in atmosphere has important effect on the reaction mechanism of the system.
同期刊论文项目
同项目期刊论文
Preliminary study on photocatalytic degradation of methyl orange and Cr(VI) compound system by titan
Photocatalytic oxidation of methyl orange over titania-bearing blast furnace slag photocatalysts and
Preparation of UV-visible light responsive photocatalyst from titania-bearing blastfurnace slag modi
Preparation and characterization of Zn/Ce/SO42--doped titania nano-materials with antibacterial acti
Preparation and Characterization of Zinc and Cerium Co-doped Titania Nano-materials with Antibacteri
A new process of gas-based direct reduction electric furnace smelting separation for high chromium v
Preparation and characterization of carbon or/and boron-doped titania nano-materials with antibacter
期刊信息
位置：