中文摘要：
以高钛渣、硅灰和高铝矾土熟料为原料,采用碳热还原氮化法合成TiN/O′-Sialon导电陶瓷粉体。利用XRD、SEM和EDS检测手段研究合成温度及恒温时间对粉体相组成和显微形貌的影响,并探讨合成机理。结果表明：随合成温度的升高和恒温时间的延长,产物中O′-Sialon的含量逐渐增加,并在1 375~1 400℃、恒温7 h时成为产物主晶相,此时产物中还有较多TiN和少量β′-Sialon生成。继续提高温度和延长反应时间,体系气氛的改变导致O′-Sialon迅速向β′-Sialon转化。合成粉体中O′-Sialon晶粒多呈等轴状,粒度约2μm,TiN晶粒为细小粒状。此外,反应体系中还有大量白色β′-Sialon晶须状沉积物生成。
英文摘要：
Electroconductive TiN/O＇-Sialon ceramic powders were synthesized by a carbothermal reduction-nitridation （CRN） method using high-titania slag, silicon fume and bauxite chalmette as the starting materials. The influences of synthesis temperature and holding time on the phase compositions and microstructures of the synthesized products were determined by XRD, SEM and EDS, and the synthesis mechanism was discussed. The results show that the content of O＇-Sialon increases gradually with the increase of synthesis temperature and holding time. The content O＇-Sialon reaches the maximum in the range of 1 375-1 400℃ at a holding time of 7 h, under which the crystalline phases also include TiN and small amount β＇-Sialon. With further increase in the synthesis temperature and holding time, the atmosphere of the reaction system makes O＇-Sialon rapidly converted to β＇-Sialon. The equiaxed O＇-Sialon grains are about 2 μm and fine TiN particles are observed in the synthesized powders. Moreover, a mass of the white whisker shape sediments appear on the surface of the samples and the inner wall of the crucible.
同期刊论文项目
同项目期刊论文
Vanadium-titanium magnetite ore blend optimization for sinter strength based on iron ore basic sinte
Influence of MgO in the form of magnesite on properties and mineralogy of high-Cr vanadium and titan
Sintering behaviors and consolidation mechanism of high-chromium vanadium and titanium magnetite fin
Preliminary study on photocatalytic degradation of methyl orange and Cr(VI) compound system by titan
Photocatalytic oxidation of methyl orange over titania-bearing blast furnace slag photocatalysts and
Preparation of UV-visible light responsive photocatalyst from titania-bearing blastfurnace slag modi
Preparation and characterization of Zn/Ce/SO42--doped titania nano-materials with antibacterial acti
Preparation and Characterization of Zinc and Cerium Co-doped Titania Nano-materials with Antibacteri
A new process of gas-based direct reduction electric furnace smelting separation for high chromium v
Preparation and characterization of carbon or/and boron-doped titania nano-materials with antibacter
期刊信息
位置：