中文摘要：
通过热重实验获得了873、973和1173K三个温度条件下不同组成的H2-CO混合气体还原氧化亚铁的动力学曲线，发现在873和973K时由于析碳反应的发生，动力学曲线较为混乱，没有规律，而在1173K时，还原曲线则随还原气体中H2含量（体积分数）的增加表现出明显的规律性．通过H2-CO与H2-Ar气体还原氧化亚铁动力学的比较，混合气体中CO参与反应的速率与其含量（体积分数）基本符合线性关系．还原产物形貌观察的结果表明，随着反应温度的升高，还原产物孔隙增大，铁相充分发育长大并逐渐有明显的烧结现象．
英文摘要：
The reduction kinetic curves of FeO powder by H2 - CO mixture with different hydrogen content at 873, 973 and 1173 K were obtained through TG experiments. It was showed that the kinetic curves at 873 and 973 K are irregular due to the carbon deposition, and the kinetic curves at 1173 K keep a certain regularity with increase of hydrogen content in H2 - CO mixture. Compared the reduction kinetics by H2 - CO and H2 - Ar mixtures, the reduction rate of CO in H2 - CO mixture and CO content （ volume fraction） is basically a linear one. Morphology observation results of the samples showed that with increase of temperature, porosity of the reduction product increases, iron phase fully develops and there is an obvious sintering phenomenon happened.
同期刊论文项目
同项目期刊论文
A model for estimating the rate constant between CO2-CO gas and molten slag containing iron oxides u
Simulation Study on Performance of Z-path Moving-fluidized Bed for Gaseous Reduction of Iron Ore Fin
Defluidization behavior of iron powders at elevated temperature: Influence of fluidizing gas and par
Preliminary study on photocatalytic degradation of methyl orange and Cr(VI) compound system by titan
Photocatalytic oxidation of methyl orange over titania-bearing blast furnace slag photocatalysts and
Preparation of UV-visible light responsive photocatalyst from titania-bearing blastfurnace slag modi
Preparation and characterization of Zn/Ce/SO42--doped titania nano-materials with antibacterial acti
Preparation and Characterization of Zinc and Cerium Co-doped Titania Nano-materials with Antibacteri
A new process of gas-based direct reduction electric furnace smelting separation for high chromium v
Preparation and characterization of carbon or/and boron-doped titania nano-materials with antibacter
期刊信息
位置：