中文摘要：
研究在含铬型钒钛矿烧结过程中MgO对烧结矿转鼓强度（TI）及低温还原粉化指数（RDI）的影响,采用熔点熔速仪和SEM-EDS研究MgO对含铬型钒钛矿熔化特性的影响,并探讨MgO在烧结过程的迁移行为。结果表明：当MgO含量为1.95%-2.63%（质量分数）时,MgO含量的提高对含铬型钒钛矿熔化特性未产生不利影响;当MgO含量由1.95%增加到2.63%时,烧结矿转鼓强度由50.33%提高到53.40%,RDI＋3.15由80.57%上升到82.71%;MgO的迁移主要以Mg2＋的形式通过类质同象形式取代Fe^2＋而形成含镁磁铁矿（Fe,Mg）O·Fe2O3,Mg^2＋的含量随着MgO含量的提高而增多,其迁移历程为：Fe O·Fe2O3→（Fe,Mg）O·Fe2O3→（Mg,Fe）O·Fe2O3→MgO·Fe2O3。
英文摘要：
The influences of MgO on the tumbler index （TI）, reduction degradation index （RDI） and melting characteristics of V-Ti-Cr magnetite sinter were studied. The transference and interaction mechanism of MgO in sintering of V-Ti-Cr magnetite were investigated by melting point-rate measuring and SEM-EDS. The results show that, when MgO content （mass fraction） increases from 1.95%to 2.63%,the melting characteristic of V-Ti-Cr magnetite does not become worse. Furthermore, TI increases from 50.33%to 53.40%and RDI＋3.15 increases from 80.57%to 82.71%with increasing MgO content from 1.95%to 2.63%. The transference of MgO is mainly in the form of Mg^2＋, which diffuses into crystal lattice of magnetite and forms （Fe, Mg）O·Fe2O3,and the content of Mg^2＋ in magnetite increases with increasing MgO content. The course of transference of MgO is FeO→Fe 2 O 3→（Fe, Mg）O→Fe 2 O 3→（Mg, Fe）O→Fe 2 O 3→MgO→Fe2O3.
同期刊论文项目
同项目期刊论文
Vanadium-titanium magnetite ore blend optimization for sinter strength based on iron ore basic sinte
Influence of MgO in the form of magnesite on properties and mineralogy of high-Cr vanadium and titan
Sintering behaviors and consolidation mechanism of high-chromium vanadium and titanium magnetite fin
Preliminary study on photocatalytic degradation of methyl orange and Cr(VI) compound system by titan
Photocatalytic oxidation of methyl orange over titania-bearing blast furnace slag photocatalysts and
Preparation of UV-visible light responsive photocatalyst from titania-bearing blastfurnace slag modi
Preparation and characterization of Zn/Ce/SO42--doped titania nano-materials with antibacterial acti
Preparation and Characterization of Zinc and Cerium Co-doped Titania Nano-materials with Antibacteri
A new process of gas-based direct reduction electric furnace smelting separation for high chromium v
Preparation and characterization of carbon or/and boron-doped titania nano-materials with antibacter
期刊信息
位置：