通过EPMA、金相等分析手段,对块状Fe2O3在1073~1273 K的氢还原过程进行了研究.结果表明,氢还原块状Fe2O3的过程具有阶段性并具有明显的分层现象,并根据XRD及EPMA检测结果分析了中间产物层的形成机理.本实验条件下,反应过程处于气体内扩散与界面化学反应控速的阶段,反应的表观活化能为27.0±5.9 kJ/mol.
英文摘要：
The hydrogen reduction process of block hematite in 1073-1273 K was studied by using EPMA and metallographic analysis. The results showed that there were a staged character and stratification in the hydrogen reduction process of block hematite. The mechanism of the staged character and stratification was discussed based on the results of XRD and EPMA. Under the experimental conditions in this work, the reduction rate was controlled by gas diffusion and inteffacial chemical reaction, and the apparent activation energy was 27.0±5.9 kJ/mol.
同期刊论文项目
同项目期刊论文
Preliminary study on photocatalytic degradation of methyl orange and Cr(VI) compound system by titan
Photocatalytic oxidation of methyl orange over titania-bearing blast furnace slag photocatalysts and
Preparation of UV-visible light responsive photocatalyst from titania-bearing blastfurnace slag modi
Preparation and characterization of Zn/Ce/SO42--doped titania nano-materials with antibacterial acti
Preparation and Characterization of Zinc and Cerium Co-doped Titania Nano-materials with Antibacteri
A new process of gas-based direct reduction electric furnace smelting separation for high chromium v
Preparation and characterization of carbon or/and boron-doped titania nano-materials with antibacter
期刊信息
位置：