中文摘要：
以2D Cf/SiC为基底材料,采用浆料刷涂工艺制得Ba0.25Sr0.75Al2Si2O8（BSAS）环境障碍涂层,并研究了未涂覆BSAS涂层（Cf/SiC）和涂覆BSAS涂层（Cf/SiC-BSAS）的两种试样的耐水腐蚀性能.结果表明：采用浆料刷涂工艺涂覆,在高纯氩气保护气氛下,经1350℃高温烧结,可在Cf/SiC试样上制得致密且无明显缺陷的BSAS涂层,一次涂覆烧结的厚度约为15μm,三次涂覆烧结涂层的厚度可达50μm;在1250℃、50%H2O-50%O2、常压静态气氛下腐蚀100h后,Cf/SiC试样的重量和抗弯强度均发生明显下降,Cf/SiC-BSAS试样的重量基本不变,强度保持率高达90%以上.
英文摘要：
Ba0.25Sr0.75Al2Si2O8（BSAS） as environmental barrier coating（EBC） was coated on the 2D Cf/SiC substrate using slurry-brushing process.The water-vapor corrosion resistance of Cf/SiC and Cf/SiC-BSAS were studied in 50%H2O-50%O2 water vapor under atmospheric pressure and static atmosphere at 1250℃,respectively.The results show that the dense BSAS coating with free cracks can be prepared by slurry-brushing method followed by heat-treatment at 1350℃ in high purity argon.The coating thickness approximate to 15μm after pasted once,and can reach 50μm after pasted for three times.The weight and flexural strength of Cf/SiC-SiC decreases greatly,while the weight of Cf/SiC-BSAS has no obvious change and the flexural strength retention is over 90% after corroded for 100 h.
同期刊论文项目
同项目期刊论文
Mechanisms of Mono-Vacancy and Oxygen Permeability in Y2SiO5 Orthosilicate Studied by First-Principl
Theoretical Prediction of Elastic Stiffness and Minimum Lattice Thermal Conductivity of Y3Al5O12, YA
Raman spectrometry study of phase stability and phonon anharmonicity of Al3BC3 at elevated temperatu
Fabrication and Water-vapor Corrosion Resistance of Ba0.25Sr0.75Al2Si2O8 Environmental Barrier Coati
Oxidation behaviour of two-dimensional C/SiC modified with self-healing Si-B-C coating in static air
Mechanism of intrinsic point defects and oxygen diffusion in yttrium aluminum garnet: First-principl
An Investigation of Environment Barrier Coating on 2D C/SiC Composites Prepared by Liquid Phase Proc
Synthesis and structure-property relationships of a new family of layered carbides in Zr-Al(Si)-C an