中文摘要：
以NazSiO3·9H2O为原料，浓H2sO4为酸试剂，采用化学沉淀法制备纳米二氧化硅，讨论Na2SiO3浓度、搅拌速度、pH值、分散剂Na2S04和表面活性剂聚乙二醇等因素对产物特性的影响，并用红外光谱、透射电镜、扫描电镜和X射线衍射等分析手段对二氧化硅纳米颗粒进行结构和形貌表征。利用本体聚合法制备了聚甲基丙烯酸甲酯一纳米二氧化硅复合材料，研究纳米二氧化硅颗粒对聚甲基丙烯酸甲酯材料力学性能的增强作用以及透光度的影响。结果表明：二氧化硅纳米粒子呈球形，粒径在50～100nm范围内、分布均匀、呈无定形；填充纳米二氧化硅的复合材料的冲击强度和弯曲强度明显提高。
英文摘要：
Silica nano-particles were prepared via chemical precipitation using Na2SiO3.9H20 and H2SO4. The effects of several technical factors on the properties of silica powders, such as Na2SiO3 concentrations, pH, agitation speed, dispersant Na2SO4 and surfactant PEG were studied. FT-IR, TEM, SEM and XRD were used to characterize the structure and morphology of the silica powders. The polymethylmethacrylate （PMMA） -silica nano-composites were prepared by in-situ bulk polymerization after silica nano-particles mixing with methylmethacrylate （MMA） monomer through ball milling. Finally, the reinforcing effect and the transparence of PMMA slices of silica nano-particles on PMMA were also investigated. The results showed that the as-prepared SiO2 particles were amorphous, spherical with uniform size distribution and the particles size could be controlled in the range from 50 to 100 nm. The impact strength and flexural strength of the composite materials filled SiO2 nano-particles was improved obviously.
同期刊论文项目
同项目期刊论文
Pt-Sn-based catalyst';s intensification using Al(2)O(3)-SAPO-34 as a support for propane dehydrogena
Improvement of oil adsorption performance by a sponge-like natural vermiculite-carbon nanotube hybri
HEXENE CATALYTIC CRACKING OVER 30% SAPO-34 CATALYST FOR PROPYLENE MAXIMIZATION: INFLUENCE OF REACTIO
High selectivity production of propylene from n-butene: Thermodynamic and experimental study using a
Direct synthesis of a fluidizable SAPO-34 catalyst for a fluidized dimethyl ether-to-olefins process
In situ synthesis of SAPO-34 crystals grown onto alpha-Al2O3 sphere supports as the catalyst for the
Thermodynamic, hydrodynamic, particle dynamic, and experimental analyses of silica nanoparticles syn
Preparation and characterization of silica-coated Fe3O4 nanoparticles used as precursor of ferroflui
Preparation and characterization of Fe3O4/polystyrene composite particles via inverse emulsion polym
Preparation, characterization and MRI application of carboxymethyl dextran coated magnetic nanoparti
Synthesis of monodisperse magnetite nanoparticles via chitosan-poly(acrylic acid) template and their
期刊信息
位置：