中文摘要：
将V-Nb-Mo微合金钢在1200℃固溶处理0.5 h后淬火,然后在不同的温度（500—650℃）回火4 h,或在650℃回火不同时间,用显微硬度判定等温回火和等时回火时析出碳化物强化机制的转变点,用三维原子探针（3DAP）表征碳化物的析出特征,并测量其等效半径r_p.根据第二相与位错交互作用的强化理论,共格应变强化主导切过机制,计算了位错切过向绕过机制转变时第二相的尺寸.结果表明,3DAP测量和强化理论计算得到的第二相的临界转变半径十分吻合,约为1 nm,表明用共格应变强化切过机制可以很好地预测析出强化作用最显著时第二相的尺寸.
英文摘要：
Precipitation strengthening can occur by means of two mechanisms,depending on the size.First,the shearing mechanism is active for small precipitates and the strengthening increases with the increase in the precipitate size.Second,the Orowan bypass process,where dislocation loops around precipitates is active for larger precipitates and the strengthening decreases with increase in the precipitate size.Therefore,there must exists a critical transition size of precipitates, in which the strengthening reaches the maximum.V-Nb-Mo micro-alloyed steels were isochronally tempered for 4 h at different temperatures and isothermally tempered for different times at 650℃ fter solution treatment at 1200℃ for 0.5 h.The tempering conditions where the transition of precipitate strengthening mechanism occurred could be ascertained by the isochronal and isothermal hardness curves.The critical transition size of precipitates was determined to be about 1.0 nm by three dimensional atom probe（3DAP）.Based on the precipitation strengthening theory and shearing mechanism dominated by coherency strengthening,the critical transition size of precipitates was calculated to be about 1.0 nm,which was in good agreement with the value measured by 3DAP.It indicates that the size of second phase can be well predicted by the precipitation strengthening theory when the micro-alloy steel reaches the maximum precipitation strengthening effect.
同期刊论文项目
同项目期刊论文
The effect of nanostructural hierarchy on the mechanical properties of aluminium alloys during defor
First principles study of Al and Ni segregation to the alpha-Fe/Cu (100) coherent interface and thei
Theoretical prediction of mechanical stability of ferromagnetic FCC Fe-Cu alloys from first principl
Molecular Dynamics Study of the Response of Nanostructured Al/Ni Clad Particles System under Thermal
Strengthening effect of Cu-rich phase precipitation in 18Cr9Ni3CuNbN austenitic heat-resisting steel
Combination of TEM and 3D atom probe study on the microstructure and alloy carbide in a Nb-V micro-a
Comparative Study on Austenite Decomposition and Copper Precipitation during Continuously Cooling Tr
The precipitation strengthening behavior of Cu-rich phase in Nb contained advanced Fe-Cr-Ni type aus
Structure and elastic property of nanosized complex oxide particles in ferritic/martensitic alloy: A
The water effect on the structural, electronic and photocatalytic properties of graphitic carbon nit
Density functional theory study of the influence of Ti and V partitioning to cementite in ferritic s
3D atom probe characterization of temporal evolution of precipitates in aging Nb-V micro-alloyed ste
Compositional and structural characterization of alloyed carbide by 3D atom probe and high-resolutio
Effects of deuterium implantation and subsequent electron irradiation on the microstructure of Fe-10
期刊信息
位置：