中文摘要：
以固相法合成的K_0.5Na_0.5NbO_3（KNN）粉体基料，熔盐法合成的片状Sr_2Bi_4Ti_5O_18晶粒为模板，采用水系流延法制备织构化KNN无铅压电陶瓷，研究了烧结温度对材料性能的影响。发现烧结温度对陶瓷的体积密度、线收缩率、织构度和压电性能均有重要影响。随着烧结温度的升高，压电性能逐渐提高，1120℃时达到最大值。其中平行于流延方向的压电常数d_33达到113 pC/N，平面机电耦合系数k_p为39.4%，介电常数ε^T_33/ε_0为486；而垂直于流延方向d_33只有82 _pC/N，k_p为35.5%，介电常数ε^T33/ε_0为456，显示出明显的各向异性。
英文摘要：
In this paper, K_0.5Na_0.5NbO_3 （KNN） synthesized by solid state reaction as base materials, flake Sr_2Bi_4Ti_5O_18 grain prepared by molten salt synthesis method as template, the KNN textured lead-free piezoelectric ceramic was prepared by aqueous tape-casting technique, and the effect of sintering temperature on the performance was studied. The results showed that the sintering temperature has very important inlfuence on the linear shrinkage, bulk density, texturing and piezoelectric properties. With the increase of sintering temperature, the performance increases and reaches maximum at 1120℃ and then decreases. In the parallel tape-casting direction, the piezoelectric constant d_33 reaches 113 pC/N, the planar electromechanical coupling coefifcient k_P is 39.4%, the dielectric constant ε^T_33/ε_0 is 486; and at the perpendicular direction, the d_33is only 82 pC/N, the kP is 35.5%, and the ε^T_33/ε_0 is 456, showing obvious anisotropy.
同期刊论文项目
同项目期刊论文
Structure and Piezoelectric Properties of (K,Na)NbO3 Ceramics Fabricated from Microwave Hydrothermal
Synthesis of Single-Crystalline Plate-shaped K0.5Na0.5NbO3 Particles by Multi-step Molten Salt Metho
Enhanced Piezoelectric Properties of (Na0.535K0.485)0.905Li0.095(Nb0.94Ta0.06)O3-(Na0.5Bi0.5)TiO3 Le
Phase transition and electrical properties of LiNbO3-modified K0.49Na0.51NbO3 lead-free piezoceramic
Microstructure, phase transition and electrical properties of LiSbO3-doped (K0.49Na0.51)NbO3 lead-fr
期刊信息
位置：