中文摘要：
利用传统熔融-淬冷工艺制备了65GeS2-15Ga2S3-（20-x）CsCl-xCsI（x=0,5,10,15,20）系列硫卤玻璃;通过测试该系列玻璃样品的密度、显微硬度、可见/近红外吸收光谱、红外透射光谱、喇曼谱、XRD衍射谱、玻璃转变温度等,对其进行了系统研究.结果表明：该系列玻璃具有较宽的成玻范围,在0.4212μm范围内具有良好的透过率;随着CsI含量（mol%）的增加,玻璃的密度逐渐增大;随着CsCl含量（mol%）的增加,光学带隙以及硬度逐渐增大;玻璃样品的玻璃转变温度随Cl-、I-的共掺比例发生明显变化,当Cl-（mol%）：I-（mol%）=1时,玻璃转变温度最低.
英文摘要：
A series of 65GeS2-15Ga2S3-（20-x）CsCl-xCsI（x=0,5,10,15,20）chalcogenide glasses were prepared by the traditional melt-quenching method.By means of the measurement of the density,microhardness,Visible-Near Infrared absorption spectra,Infrared optical transmission spectra,Raman spectra,X-ray diffraction curves and glass transition temperature Tg,the optical characters of this kind of glasses were studied systematically.The results show that,the series of glass samples have a wide composition range of glass formation and a good transparency in the entire 0.4212μm spectral region.With increasing of the content of the CsI,the density increases progressively.With increasing of the content of the CsCl,the optical band gap and microhardness increase gradually.Tgof glass samples changes with the change of the molar ratio of Cl-/I-.When the ratio located at 1,Tghits its rock bottom.
同期刊论文项目
同项目期刊论文
Glass formation and third-order optical nonlinear characteristics of bismuthate glasses within Bi2O3
Competitive Phase Separation to Controllable Crystallization in 80GeS2 center dot 20In2S3 Chalcogeni
Performance improvement of transparent germanium-gallium-sulfur glass ceramic by gold doping for thi
Competitive Phase Separation to Controllable Crystallization in 80GeS 2·20In 2S 3 Chalcogenide Glass
Modeling and simulation of mid-IR amplifying characteristics of Tm3+-doped chalcogenide Photonic Cry
Tapered chalcogenide-tellurite hybrid microstructured fiber for mid-infrared supercontinum generatio
Mechanism of the enhancement of mid-infrared emission from GeS2-Ga2S3 chalcogenide glass-ceramics do
期刊信息
位置：