中文摘要：
为了研究裂隙岩体在水作用下的损伤断裂机制，考虑水产生的垂直裂纹面的静水压力和平行裂纹面的拖拽力，分析处于压剪和拉剪状态的单裂纹应力状态，推导出水作用下裂纹的应力强度因子。还定义基于断裂韧度的损伤变量，并将损伤变量引入Dugdale裂纹模型，推导出水损伤作用下压剪和拉剪应力状态下裂纹的应力强度因子。基于压剪条件下的断裂准则和最大周向应力理论，推导出压剪和拉剪应力状态下，考虑水损伤作用的裂隙岩体断裂准则。
英文摘要：
In order to study damage fracture law of fissured rock masses, the hydrostatic pressure vertical to crack surface and drag force parallel to crack surface were taken into consideration, both of which are generated by water action. Stress condition of single crack under compressive-sheafing stress condition and tensile-shearing stress condition were calculated respectively. And the stress intensity factor during water action was deduced. A new damage variable related to fracture toughness was presented and the new damage variable was introduced into Dugdale crack model, and the stress intensity factor of compressive-shearing crack and tensile-sheafing crack were deduced respectively. Finally, fracture criterion of fractured rock mass considering water damage action was presented, under compressive-shearing stress condition and tensile-sheafing stress condition respectively, based on the compressive-shearing fracture criterion and the maximum hoop stress theory.
同期刊论文项目
同项目期刊论文
Testing study on damage and fracture mechanical effects for swelling soft rock during water corrosio
Fracture test and failure mechanism of rock-like material of relatively different fracture apertures
Micromechanical model for equivalent crack propagation under chemical corrosion of water-rock intera
Time-dependence of damage and fracture effect for strain softening of soft rock under water corrosio
Size effect experimental study of strength and deformation in different height-to-diameter ratio sof
Failure mechanism and its simplified models of brittle material with ordered multi-fissures under un
Study of fracture damage evolution mechanism of compression-shear rock cracks under high seepage pre
Improved nonlinear viscoelasto-plastic rheological model of rock and its correction of hardening coe
Sequential Indentation Tests to Investigate theInfluence of Confining Stress on Rock Breakage by Tun
Numerical simulation on effects of embedded crack on rock fragmentation by a tunnel boring machine c
Mechanical Behavior of Brittle Rock-Like Specimenswith Pre-existing Fissures Under Uniaxial Loading: