中文摘要：

以膨润土为原料，经硫酸处理后得到层状结构明显的矿物材料，通过制浆干燥的方法向层间有效插入Na＋，制备了在室温下具有较高离子电导率的固体电解质。考察了矿物材料的微观结构、Na＋含量及含水量对矿物材料电导率的影响，并用扫描电镜、能谱、红外光谱和x射线衍射对其结构进行了表征，结果表明，此法制备的膨润土矿物电解质材料在常温下离子电导率最高可达到7．81×10^-4S·cm-1，比传统的高温固相法提高了2倍。

英文摘要：

The bentonite minerals have been used to prepare solid-state electrolyte with high con- ductivity at room temperature. At first,bentonite was leached by H2SO4 ,and then obtained min- erals materials with regular and obvious layered structure that can be inserted lots of Na＋ effec- tively by slurry-making-and-drying method. The effects of microstructures, Na＋ content, water content on conductivity of minerals materials were studied, and the structure was characterized by scanning electron microscope （SEM）, energy spectrum （EDS）, Fourier transform-infrared spectra （FTIR） and X-Ray diffraction （XILD）. The result indicated that bentonite minerals electrolyte have a maximum value of 7.81 ×10^-4S·cm- at room temperature, the value of conductivity is 2 times of the prepared by the high temperature solid state reaction.