采用连续共沉淀与喷雾干燥成型技术相结合的方法制备了微球状Fe/Cu/K/Al2O3催化剂,结合TG、N2物理吸附、XRD、H2-TPR、CO-TPR、Mssbauer谱等表征手段,研究焙烧温度对Fischer-Tropshc（F-T）合成铁基催化剂的结构性质、还原行为和碳化行为的影响.结果表明,较高的焙烧温度有利于碳酸盐的分解和结晶水的脱除,促进了催化剂的还原.随着焙烧温度的进一步升高,催化剂的比表面积减小,平均孔径增大,α-Fe2O3晶粒的粒径增大,催化剂中金属与载体的相互作用增强,从而削弱了CuO、K2O助剂的作用,严重抑制了催化剂的还原和碳化.
英文摘要：
An Fe/Cu/K/Al2O3 catalyst for Fischer-Tropsch synthesis （FTS） was prepared by using a combination of co-precipitation and spray-drying method. Thermal gravity （TG）, N2 physisorption, X-ray diffraction （XRD）, H2 temperature programmed reduction （H2-TPR）, CO temperature programmed reduction （CO-TPR）, and Mossbauer effect spectroscopy （MES）, were used to investigate the effects of different calcination temperatures on the structural properties, reduction, and carburization behaviors of the iron-based catalyst. The results indicated that an increase in calcination temperature facilitated the carbonate decomposition and H2O removal and promoted the reduction of the catalyst. With further increasing the calcination temperature, the BET surface area of the catalyst decreased, and the size of the catalyst crystallite and the average pore diameter increased. Furthermore, high calcination temperature enhanced the metalsupport interaction, which weakened the promotional effect of CuO and K2O, and therefore, severely suppresseed the reduction and carburization behaviors of the catalyst.
同期刊论文项目
同项目期刊论文
Phase transformations of a spray-dried iron catalyst for slurry Fischer-Tropsch synthesis during act
Effect of interaction between potassium and structural promoters on Fischer-Tropsch performance in i
Formation of CHx species from CO dissociation on double-stepped Co(0001):exploring Fischer-Tropsch m
Effect of reduction pressure on precipitated potassium promoted iron-manganese catalyst for Fischer-
Density Functional Theory Study of Triangular Molybdenum Sulfide Nanocluster and CO Adsorption on It
Effect of air-exposure on reduction behavior of a Fe–Mn–Cu–K/SiO2 Fischer-Tropsch synthesis catalyst
Effect of ZrO2 promoter on structural change of Co/SiO2 catalyst during its deactivation in F-T synt
Isothermal kinetics modelling of the Fischer-Tropsch synthesis over the spray-dried Fe-Cu-K catalyst
Preparation and catalytic activity for Fischer-Tropsch synthesis of Ru nanoparticles confined in the
Effect of catalyst pore size on the catalytic performance of silica supported cobalt Fischer-Tropsch
期刊信息
位置：