中文摘要：
以甲苯二异氰酸酯、聚L--醇、丙烯酸羟乙酯为反应物，并以乙二醇或1，3-丁二醇为扩链剂，合成了扩链型聚氨酯丙烯酸酯，并以其制备了uV固化涂料。研究了聚乙二醇及扩链剂对uV固化涂膜性能的影响。随聚乙二醇相对分子质量的增加，涂膜的柔韧性从4．9mm变为2．0mm，硬度从H降低为6B；扩链温度在25～30℃之间时，扩链反应容易控制。扩链后涂膜的表干时间变长，附着性变好，柔韧性小于1mm，同时涂膜耐水性、耐酸性、耐碱性、耐磨性、耐溶剂性均有所提高。
英文摘要：
A chain-extending UV-curable polyurethane acrylate （PUA） was synthesized with toluene diisocyanate （TDI）, polyethylene glycol （PEG）, hydroxyethyl acrylate （ HEA）, and chain extender ethylene glycol or 1,3-butanedio. The effects of PEG and chain extender on the cured film properties of the UV-cured PUA coatings were investigated. With the increase of the PEG molecular weight, the flexibility of the cured film was changed from 4. 9 mm to 2 mm, and the hardness was decreased from H to 6B. The chain-extension reaction can be easily con- trolled between 25-30℃.Compared with non chain-extending UV-PUA, the dust-free time of the chain-extending UV-PUA was increased, the adhesive force was improved, and the flexibi- lity was smaller than 1 mm. The water resistance, acid resistance, alkali resistance, heat resistance, wearing resistance and solvent resistance of the cured film were improved.
同期刊论文项目
同项目期刊论文
An Attempt of Improving Polyester Inkjet Printing Performance by Surface Modification using β-Cyclod
Dispersibility and Hydrophobicity Analysis of Titanium Dioxide Nanoparticles Grafted with Silane Cou
Surface Deposition on Cellulose Substrate via Cationic SiO2/TiO2 Hybrid Sol for Transfer Printing Us
Preparation and Characterization of PAM/SA Tough Hydrogels Reinforced by IPN Technique Based on Cova
Gelation Performance of Cationic Gemini Silica Sol with Inorganic Salts and Its Antibacterial Proper
Organic-inorganic hybrid silica film coated for improving resistance to capsicum oil on natural subs
Alterable Superhydrophobic-Superhydrophilic Wettability of Fabric Substrates Decorated with Ion-TiO2
Preparation and Photochromic Properties of Nanocapsules Containing Azo Compound with Polyurethane as
A foam single-face pretreatment to modify silk fabric using EBODAC to improve inkjet printing perfor
Anthraquinone chromophore covalently bonded blocked waterborne polyurethanes: synthesis and applicat
Covalent bonding and photochromic properties of double-shell polyurethane-chitosan microcapsules cro
The electric response behavior and microencapsulation of the pigment phthalocyanine green G using in
Water-soluble cationic chitosan derivative to improve pigment-based inkjet printing and antibacteria
An attempt of improving polyester inkjet printing performance by surface modification using ss-cyclo
UV-Vis Irradiation Fatigue Resistance Improvement of Azo Photochromic Compound Using Polyurethane-Ch
Sol-gel synthesis and characterizations of organically modified silica coatings on knitted cellulose
期刊信息
位置：