中文摘要：
应用已发明的MHA黏结剂替代膨润土制备钒钛磁铁矿氧化球团,获得质量优良的高炉冶炼原料。研究表明：当MHA用量为0.25%,在预热温度950℃,预热时间10 min,焙烧温度1 250℃,焙烧时间10 min的条件下,获得的预热球团抗压强度为522 N/个,焙烧球团抗压强度为3 702 N/个。与2.0%膨润土球团矿比较,MHA成品球团的抗压强度略低,而TFe品位明显提高1.11%。2种黏结剂球团矿的还原性能指标接近。MHA球团黏结剂在氧化球团矿生产中具有良好的应用前景。
英文摘要：
MHA invented by Central South University was used as an alternative binder of bentonite for oxidized pellet preparation from vanadium, titanium- （V, Ti-） bearing magnetite concentrates, and high-quality blast furnace burdens were obtained. Final results show that preheated pellets with 522 N/P compressive strength and roasted pellets with 3 702 N/P compression strength are achieved, under conditions that MHA dosage is 0.25%, preheating temperature is 950 ℃, preheating time is 10 min, roasting temperature is 1 250 ℃ and roasting time is 10 min. Compared 0.25% MHA pellets with 2.0% bentonite pellets, compression strength of MHA pellets is a little lower, while content of total iron （TFe） of them increases by 1.11%. The reducibility performance index of two kinds of roasted pellets is approximate. MHA binder has good application prospect in the oxidized pellets production.
同期刊论文项目
同项目期刊论文
Structure characteristics and adhesive property of humic substances extracted with different methods
A further study on the interaction between one of organic active fractions of the MHA binder and iro
期刊信息
位置：