中文摘要：

用MM-200型摩擦磨损试验机考察了了射线辐照对酚酞聚芳醚酮（PEK-C）的摩擦磨损性能的影响，用SEM观察了摩擦表面和磨屑的形貌。结果表明：经辐照后，PEK-C的耐磨损性能下降；随着辐照剂量的增大，PEK-C摩擦因数几乎保持不变，而磨损率呈上升趋势；未辐照试样的磨屑为较小的片状，而辐照后的磨屑为较大的片状，这一现象与材料磨损程度的大小相对应。

英文摘要：

The effect of y irradiation on the friction-wear properties of polyetherketone with cardo group （PEK-C） was studied with a model MM-200 friction and wear tester. The morphology of worn surfaces and wear debris of PEK-C was observed by SEM. The anti-wear performance of PEK-C deteriorated after being y irradiated. With the increasing radiation dose, the friction coefficient of PEK-C was almost invariable, but the wear rate of PEK-C increased. The size of wear debris of the PEK-C composites being radiated was bigger than that of normal PEK-C composites. This was corresponding to the degree of wear of PEK-C.