中文摘要：
以二苯甲酮（BP）为光引发剂、丙酮和水的混合物为溶剂,研究了室温下多官能单体三羟甲基丙烷三丙烯酸酯（TMPTA）在低密度聚乙烯（LDPE）表面的光接枝聚合（λ＞300nm）.研究表明,多官能单体的接枝速率较快,接枝聚合易产生交联结构,聚合后仍残留双键;延长聚合反应时间、增加单体用量有利于单体接枝转化率的提高;随引发剂用量增加,单体接枝转化率出现一峰值;在研究范围内,混合溶剂中水含量增加可使单体接枝转化率明显提高.扫描电镜观察到接枝膜表面形成了许多小球,表面粗糙度增加,疏水性提高.
英文摘要：
Photografting （≥ 300 nm） of trimethylol propane triacrylate （TMPTA） onto the surface of low-density polyethylene （LDPE） films was investigated at room temperature in a mixed solvent composed of acetone and water, using benzophenonc （BP） as an initiator. It seems that the surface, forming a cross-linked structure, and as confirmed polyfunctional monomer could be grafted easily onto the by IR spectroscopy there were still some double bonds un-reacted. Influences on the photografting of TMPTA were examined and the experimental results indicated that longer irradiation time and higher monomer concentration were useful for the increase of grafted polymer conversion. At a certain concentration of BP, a maximum grafted polymer conversion was obtained, and the decrease of grafted conversion at higher BP concentrations was probably due to the absorption effect of initiator. The increase of grafted polymer conversion was observed with increasing the water contents. SEM images showed that a lot of small particles appeared on the surface of grafted films, and water contact angle measurements noted that the surface hydrophobicity was improved.
同期刊论文项目
同项目期刊论文
Fabrication of a molecular-level multilayer film on organic polymer surfaces via chemical bonding as
Direct construction of monolayered large spherical functional particles onto organic material surfac
Photografting of unable-to-be-irradiated surfaces. II. Batch liquid-phase process by one-step method
A facile method for grafting polymerisation of acrylonitrile onto LDPE film with high grafting effic
Vapor phase surfase grafting polymerization of acrylonitrile onto poly(ethelene terephthalate) film.
A novel strategy for the preparation of reactively compatibilized polymer blends with oligomers cont
A novel and facile approach for preparing composite core–shell particles by sequentially initiated g
Facile surface superhydrophilic modification: NVP/MBA inverse microemulsion surface graft polymeriza
Covalently attached graft polymer monolayer on organic polymeric substrate via confined surface inhi
Thickness measurement of nanoscale polymer layer on polymer substrates by attenuated total reflectio
Synthesis of Highly Hydrophilic Polyaniline Nanowires and Sub-Micro/Nanostructured Dendrites on Poly
Using Glycidyl Methacrylate as Cross-linking Agent to Prepare Thermosensitive Hydrogels by a Novel O
The bio-inspired approach to controllable biomimetic synthesis of silver nanoparticles in organic ma
Precipitation Polymerization in Acetic Acid: Synthesis of Monodisperse Cross-Linked Poly(divinylbenz
Stabilizer-free dispersion copolymerization of maleic anhydride and vinyl acetate. I. Effects of pri
Directly fabricating monolayer nanoparticles on a polymer surface by UV-induced MMA/DVB microemulsio
One-pot fabricating superstructure polymer particles via situ-polymerization-stringed-assembly of tw
Micro/nanoscale well and channel fabrication on organic polymer substrates via a combination of phot
Synthesis of antibacterial polypropylene film with surface immobilized polyvinylpyrrolidone-iodine c
Facile Fabrication of Monolayered Hollow Submicrospheres of PANI on Surfaces of Modified Polymer Fil
A novel method for functionalization of polypropylene with oligomer of glycidyl methacrylate: charac
Synthesis of Large-Area Three-Dimensional Polyaniline Nanowire Networks via Constructing 'Soft Templ
Surface functionalization of polypropylene film via UV-induced photografting of n-vinylpyrrolidone/m
Surface photografting polymerization of vinyl acetate, maleic anhydride, and their charge-transfer c
High efficient grafting polymerization of styrene on surface of NBR latex and physical properties of
Stabilizer-free dispersion copolymerization of maleic anhydride and vinyl acetate. II. Polymerizatio
Fabrication of Shape-Controllable Polyaniline Micro/Nanostructures on Organic Polymer Surfaces: Obta
Surface photografting polymerization of trimethylolpropane triacrylate onto LDPE substrate in tetrah
Novel tin-coupled star-shaped medium vinyl butadiene rubber. I. Arm number and its effect on propert
Fabrication of a pore-connected, macroporous, crosslinked polystyrene monolith with anhydride groups
Novel tin-coupled star-shaped medium vinyl butadiene rubber. II. Vinyl content, molecular weight, an
期刊信息
位置：