中文摘要：
利用自行研制的低频振动注塑成型装置进行等规聚丙烯（iPP）试样的结构与性能研究．实验中对常规注射和振动注射成型的试样力学性能和微观形态进行了对比实验．采用低频振动注塑成型工艺实现了IPP试样的自增强，在190℃下进行注射，强度由常规试样的41.3MPa最大提高到振动试样的48.4MPa（振幅PA=59．4MPa，振频FR=0．7Hz），强度提高了17.2％；SEM显示常规试样芯层结构主要由球晶构成，振动注射使球晶在流动方向上变形、取向，晶粒尺寸得到细化；DSC表明振动注射促进熔融峰向高温漂移，晶体结晶更加完善，结晶度最大提高了12．1％；WAXD显示低频大振幅振动注塑有利于γ晶型的生成，γ晶型有利于试样实现自增强．
英文摘要：
A self-made low frequency vibration injection molding device was adopted to explore the mechanical properties and morphology for iPP injected moldings. The morphology and mechanical properties of samples produced by conventional injection molding （CIM） were used to compare with those obtained by vibration injection molding （VIM）. For VIM the main processing parameters are vibration frequency and vibration pressure amplitude, the range of vibration frequency is 0 - 3 Hz, and the range of pressure vibration amplitude is 0 - 59.4 MPa. During the injection and pressure holding stages for CIM the injection and holding pressures are always constant, but for VIM an additional pulsing pressure vibration is exerted on the melt in the runner system and mold cavity, causing compression and decompression on the melt and shearing at the melt-solid interface, and it progresses from surface to core of the dumbbell specimen during solidification stage. In this work, the isotactic polypropylene material was plasticized and pumped into the melt chamber by a single screw extruder. During injection and pressure holding stages for the VIM,the melt was vibrated about 25 s in the dumbbell specimen mould and then cooled down in about 20 s. The melt injection temperature and mould temperature are set at 190℃ and 40℃ respectively. The injection pressure for CIM and the base pressure for VIM was 39.5 MPa.The VIM samples were injected at different vibration frequencies and pressure vibration amplitudes, respectively. To prepare VIM samples treated under different vibration frequencies,the vibration pressure amplitude was set at 19.8 MPa, and for VIM samples teated under different vibration pressure amplitudes, the vibration frequency was set at 0.7 Hz. With application of melt vibration technology the mechanical properties of iPP injection moldings were improved. The tensile strength and impact strength increase with the increasing of pressure vibration amplitude, while the elongation at break decreases. The tensile strength inc
同期刊论文项目
同项目期刊论文
Simulation of nonisothermal flow of melt during melting process of vibration-induced polymer extrude
Modeling the continuous melt transesterification of bisphenol-A and diphenyl carbonate in a continuo
Analyses of dynamic rheological behavior of polymer melt based on novel experimental equipment and p
A kinetic network model for molten low-density polyethylene in parallel superposition vibration forc
The dynamic apparent viscosity of polymer melts during pulsatile extrusion flow with vibration force
Effects of vibration force field on the interfacial interaction and morphology of polystyrene/poly(m
Synergetic Effect on PP/mEPDM Blends Under Vibration Force Field in Tri-Screw Dynamic Mixing Extrude
The Preparation of Polypropylene/Wollastonite Composites with Tri-screw Dynamic Compounding Extruder
Computer-aided experiment of using real-time small angle light scattering image processing technique
Effect of Dynamic Shear on the Microcellular Foaming of Polypropylene/High-Density Polyethylene Blen
Effect of Temperature on Foaming Behaviors of Homo- and Co-polymer Polypropylene/Polydimethylsiloxan
The Effect of Concentrations of Modifying Agent and Plasticizer on Cell Morphology of PVC Microcellu
Enhancing mechanical properties and magnetic performance of plastics magnet via mixing under vibrati
期刊信息
位置：