中文摘要：
以费氏粒度为8.06μm的WC粉与Co（NO3）2·6H2O为原料,采用N（CH2CH2OH）3（TEA）为还原剂制备WC-12%Co（质量分数）包裹粉,以包裹粉为原料制备WC-12%Co硬质合金。采用扫描电镜观察包裹粉与合金中WC晶粒的立体形貌,采用X射线衍射仪分析粉末的物相组成,采用比表面积分析仪分析TEA还原产物多孔泡沫Co的比表面积,采用金相显微镜观察合金的组织结构。结果表明：包裹粉中Co为纯fcc高温相结构,呈多孔泡沫状纳米组装结构形式包裹在WC粉末表面;WC-12%Co合金组织结构均匀,平均晶粒度为4.8μm,WC晶粒结晶完整、呈规则多面体形状。
英文摘要：
The WC-12%Co（mass fraction） cemented carbide with an average grain size of 4.8 μm and homogeneous microstructure was prepared from porous spumous cobalt enwrapped tungsten carbide powders produced by a novel chemical route.The tungsten carbide powder with Fisher sub-sieve sizer granularity of 8.06 μm and cobaltous nitrate hexahydrate were used as the starting materials,and the triethanolamine（TEA） was used as the reducer.The phase constitutes and morphology of the powders were investigated by X-ray diffractometry and scanning electron microscopy,respectively.BET specific surface area analyzer was used to analyze the porous spumous cobalt reduced with TEA.The microstructure of WC-Co cemented carbide was observed by metallographic microscopy.The results show that,in the cobalt enwrapped WC powders,cobalt exists in pure face centered cubic structure in the form of nano particles assembly.The tungsten carbide grains in the alloy are characterized by regular polyhedron morphology and high degree of crystalline perfection.
同期刊论文项目
同项目期刊论文
Effect of strain rate on the compressive behaviour of a Zr56Al10.9Ni4.6Cu27.8Nb0.7 bulk metallic gla
Conversion of natural egg-shell to 3D flower-like hydroxyapatite agglomerates for highly sensitive d
Sea cucumber-like hydroxyapatite: cation exchange membrane-assisted synthesis and its application in
In situ formation of La containing dispersed phase on the sinter skin of La2O3 and Cr3C2 unitedly do
Influence of copper content on the microstructure and hardness of copperdoped tungsten carbide-cobal
Low-temperature growth of tetragonal tungsten nanowire arrays on tungsten substrate using Ni solid c
Ultrafine and nano scaled tungsten carbide synthesis from colloidal carbon coated nano tungsten prec
Directional migration behavior of cerium during the sintering process of mischmetal doped cemented c
Surface adsorption phenomenon during the preparation process of nano WC and ultrafine cemented carbi
期刊信息
位置：