中文摘要：
采用硝酸酸化-乙醚萃取法制备了一种硅钨杂多酸催化剂,应用扫描电镜（SEM）、红外光谱（FTIR）、X射线粉末衍射（XRD）、程序升温脱附（NH3-TPD）、热重分析（TG）等手段对催化剂进行了表征,并以甲醇和油酸为反应物,研究了所制备的硅钨杂多酸在催化酯化反应时的活性,考察了催化剂用量、反应时间、反应温度等反应参数对酯化反应产品收率的影响.结果表明：当甲醇与油酸的质量比为3∶2,催化剂用量为反应物总质量的1.4%,反应时间为3.5 h,反应温度为65℃时,油酸甲酯的收率最高,为96.45 wt%.
英文摘要：
The nitric acid acidification method incorporated with an ether extraction technique is used to prepare a silicotungstic heteropoly acid catalyst in this study. The resulting catalyst is characterized by scanning electron microscopy （SEM）, infrared spectroscopy （FTIR）, powder X-ray diffraction （XRD）, temperature pro- grammed desorption of ammonia（NH3-TPD） and thermogravimetric analysis （TG）. The catalytic activity of the silicotungstic heteropoly acid catalyst is studied from the esterification reaction of oleic acid and methanol. The syntheses conditions with respect to catalytic activities have been optimized individually, including the mass ratio of methanol to oleic acid, as well as the mass ratio of catalyst to reactants, reaction time and reaction temperature. Results show that when the mass ratio of methanol to oleic acid is 3：2, mass ratio of catalyst to reactants is 1.4 %, reaction time 3.5 h and reaction temperature is 65 ℃, a yield of methyl oleate 96.45 wt% is obtained from this optimal reaction condition.
同期刊论文项目
同项目期刊论文
~Phase transformation synthesis of novel Ag2O/Ag2CO3 heterostructures with high visible light effici
~Hydrothermal synthesis and characterization of novel PbWO4microspheres with hierarchical nanostruct
A sonochemical route to fabricate the novel porous F, Ce-codoped TiO2 photocatalyst with efficient p
Thermal stability, microstructure and photocatalytic activity of the bismuth oxybromide photocatalys
~Stable Au25(SR)18/ TiO2 Composite Nanostructure with Enhanced Visible Light Photocatalytic Activity
~Novel hollow Pt-ZnO nanocomposite microspheres with hierarchical structure and enhanced photocataly
~Novel noble metal (Rh, Pd, Pt)/BiOX(Cl, Br, I) composite photocatalysts with enhanced photocatalyti
~Synthesis and characterization of Ag/TiO2-B nanosquares with high photocatalytic activity under vis
~Preparation of Co/CexTi1-xO2 Catalysts and Their Catalytic Performance in the Catalytic Partial Oxi
Fast fabricate Co3O4 or CuO/BiVO4 composite photocatalysts with high crystallinity and enhanced phot
An efficient palladium membrane reactor for increase the yield of styrene in ethylbenzene dehydrogen
Preparation of bismuth oxyiodides and oxides and their photooxidation characteristic under visible/U
~Preparation, characterization and photocatalytic performance of noble metals (Ag, Pd, Pt, Rh) depos
Novel hollow Pt-ZnO nanocomposite microspheres with hierarchical structure and enhanced photocatalyt
Preparation, Characterization and Photocatalytic Performance of Ag/BiOX (X=Cl, Br, I) Composite Phot
Application of mixture topological index method to predict the dynamic viscosity of the hypothetical
Platinum nanoparticles supported on hollow mesoporous tungsten trioxide microsphere as electrocataly
期刊信息
位置：