中文摘要：
考察了辉钼精矿在微波场中的升温行为，研究了物料厚度、微波功率及物料量对辉钼精矿升温行为的影响。研究结果表明，辉钼精矿具有良好的微波吸收性能，物料在微波场中升温与微波功率呈正比关系，而与物料厚度和物料量成反比。在微波功率为2．6kW，物料厚度为2mm条件下，微波加热13min后，辉钼精矿可升温至600℃。采用微波氧化焙烧辉钼精矿是可行的。
英文摘要：
The temperature rise behavior of molybdenite concentrate in microwave fields was investigated.The influences of material thickness, microwave power, and material quantity etc.on the temperature rise behavior of molybdenite concentrate were researched.Results showed that molybdenite concentrate had good microwave absorption properties, and temperature- rising of material in microwave fields was proportional to microwave power, however, inversely proportional to both material thickness and material quantity.When materials were heated in microwave for 13 min,under the conditions of microwave power at 2.6 kW and material thickness of 2 mm,molybdenite concentrate temperature could reach 600 ℃.Therefore,it＇s feasible to roast molybdenite concentrate by adopting microwave energy.
同期刊论文项目
同项目期刊论文
Microwave absorbing characteristics and temperature increasing behavior of basic cobalt carbonate in
Optimization of combined mechanical activation-roasting parameters of titania slag using response su
Green evaluation of microwave-assisted leaching process of high titanium slag on life cycle assessme
Optimization of preparation for Co3O4 by calcination from cobalt oxalate using response surface meth
Optimization of preparing V2O5 by calcination from ammonium metavanadate using response surface meth
Optimization of processing parameters for microwave drying of selenium-rich slag using incremental i
Prediction model of ammonium uranyl carbonate calcination by microwave heating using incremental imp
Prediction model of microwave calcining of ammonium diuranate calcination using incremental improved
Study of the Optical Transmission Enhancement Properties in a One-dimensional Ag Film with Different
期刊信息
位置：