通过在我国西北格尔木典型大气环境进行大气暴露实验，测定LC4铝合金在该地区的腐蚀率：利用扫描电镜（SEM）、能量色散X射线谱（EDX）、电子探针（EPMA）、红外光谱（FTIR）和X射线衍射仪（XRD）观察分析LC4铝合金腐蚀表面形貌、元素分布和腐蚀产物结构。结果表明：LC4铝合金的腐蚀以点蚀为主要特征，比其在非盐湖大气环境中的腐蚀严重，朝地面的腐蚀比朝天面严重，腐蚀产物层中含有大量的氧和铝，较多的氯和硫：主要腐蚀产物为Al2O3，Al2O3·2SiO2·2H2O和Al2Cl6·6H2O：含氯和硫的盐参与铝合金的大气腐蚀过程，并起到促进腐蚀的作用。
英文摘要：
The corrosion behaviors of typical high-strength aluminum alloy LC4 was studied by atmospheric exposure test, combining the experimental techniques including mass loss, morphological check of samples and analysis of corrosion products. The products formed on aluminum alloy LC4 exposed for 12 months were characterized by X-ray diffractometry（XRD） and infrared transmission spectroscopy （IRS）, the results show that the main products are Al2O3, Al2O3·2SiO2·2H2O and Al2Cl6·6H2O. The surface morphology was observed by scanning electron microscopy （SEM）. The morphology of cross section of skyward surface exposed in salt lake atmosphere for 6 months and the distributions of O, Cl, S, Si and Al were analyzed by electron probe micro analyzer （EPMA）. Corrosion on field-ward surface is more severe than that on skyward surface. The character of the corrosion products is related to the abundant chloride environment.
同期刊论文项目
同项目期刊论文
期刊信息
位置：