中文摘要：
在实验室模拟条件T（25＋2）℃，相对湿度（95 ±5）％），采用增重法、扫描电子显微镜、傅立叶红外光谱和X射线衍射等方法研究氯化钠和几种模拟环境气氛对7A04铝合金大气腐蚀行为的影响，并对其腐蚀机理进行讨论。结果表明：表面沉积氯化钠的7A04铝合金在几种模拟气氛环境中均明显地加速了材料的腐蚀；随腐蚀时间的延长，腐蚀产物不断增多；腐蚀产物微观形貌呈团块状且凹凸不平；腐蚀增重△m／A与暴露时间t之间符合指数衰减规律；气氛腐蚀性由强到弱的顺序为50×10^-6 SO2〉1％CO2〉空气。
英文摘要：
The corrosion behavior of 7A04 aluminum alloy deposited with NaC1 in several simulated environments （（25±2） ℃ and relative humidity （RH） （95±5）%） was investigated by mass gain method, Fourier transform infrared spectroscope, scanning electron microscopy and X-ray diffractometry. The corrosion mechanism for aluminum alloy was discussed. The results show that NaCl can evidently accelerate the atmospheric corrosion of 7A04 aluminum alloy in several simulated environments. The corrosion products increase with prolonging corrosion time. The surface observation reveals that the corrosion products are agglomerate and accidented. The relationship between mass gain of corrosion product and time accords with the exponential attenuation rule. The corrosion sequence of corrosion mediums from strong to ebb is 50 × 10^-6 SO2〉1%CO2〉air.
同期刊论文项目
同项目期刊论文
期刊信息
位置：