中文摘要：
通过机械化学方法制备了Zn4Sb3和钇掺杂的Zn4Sb3试样.试样的相组成和相变过程分别采用X射线衍射（XRD）,扫描电镜（SEM）和差示扫描量热（DSC）方法进行研究.扫描电镜结果显示,颗粒大小随钇掺杂量增加而减少,直到（Zn1-xYx）4Sb3中钇的摩尔分数达到x=0.02.X射线衍射结果表明,当x=0.02时Zn4Sb3的百分含量达到最大.DSC结果表明,钇掺杂以后的试样球磨相同的12 h,相变温度从820 K变化到825 K,最大峰值减小.
英文摘要：
We prepare the samples of Zn4Sb3 and Y-doped Zn4Sb3 by the mechanochemical method. The phase composition and transformation in this alloy system during mechanical alloying is investigated with X-ray diffraction （XRD）, Scanning electron micrographs （SEM） and differential scanning calorimetry （DSC） respectively. The results of SEM shows that the particle size decrease with increasing of Y-doped amount untile molar fraction of Yttrium （Y） x =0.02 in （Zn1-xYx）4Sb3. XRD results indicate that the percentage composition of Zn4Sb3 become largest in x = 0.02. DSC results shows that the transition temperature alter from 820 K to 825 K and the peak area decrease after doping Y grinding the same 12 h.