中文摘要：
以自制高纯乙醇钽为原料，通过水解、干燥与煅烧生产粒度约35nm的高纯Ta2O5纳米粉。研究了水解过程中乙醇钽浓度、温度、加料时间对产品粒度的影响以及煅烧温度与时间对Ta2O5晶形的影响。选取水解最佳条件为：乙醇钽浓度1.0mol／L，水解温度50℃左右，加料时间约15min。加完后，搅拌5min，接着加入氨水溶液调节pH值到8～9，同时升温至80℃-85℃保温30min；煅烧温度800℃，时间2h。得到的Ta2O5产品粒度约35nm，纯度〉99．997％。
英文摘要：
High-purity tantalum oxide nanoparticles were prepared by using tantalum ethoxide as materials through the following three processes, such as hydrolysis, dryness and calcining. The effects of tantalum concentration, temperature and reaction time on the particle size and morphology, and the effects of temperature and calcined time on the crystalline of tantalum oxide have been investigated. The optimum conditions of hydrolysis were chose as tantalum of 1.0 mol/L, at about 50℃ for 15 min. After five minutes, the pH value was adjusted to about 8-9 by adding ammonia aqueous, at the same time, the temperature increased to about 80℃-85℃, then keeping the temperature constant for half an hour. The optimal calcining conditions were chose at 800℃ for 2 h. The tantalum oxide content is more than 99.997% and the granularity is about 35 nm.
同期刊论文项目
同项目期刊论文
Single and cooperative bioleaching of sphalerite by two kinds of bacteria - Acidithiobacillus ferrio
Preservation of Acidithiobacillus caldus: A moderately thermophilic bacterium and the effect on subs
Isolation of Phosphate-Solubilizing Fungi from Phosphate Mines and Their Effect on Wheat Seedling Gr
Large-scale Hydrothermal Synthesis and Characterization of Size-controlled Lanthanum Hydroxide Nanor
Identification and fermentation optimization of protopectinase-overproducing strain Aspergillus nige
Bioleaching of chalcopyrite concentrate by a moderately thermophilic culture in a stirred tank react
The effect of preferential flow on extraction and surface morphology of copper sulphides during heap
Comparative genomic analysis of Acidithiobacillus ferrooxidans strains using the A. ferrooxidans ATC
Isolation and identification of moderately thermophilic acidophilic iron-oxidizing bacterium and its
Characterization and Reconstitute of a [Fe4S4] Adenosine 5 '-Phosphosulfate Reductase from Acidithio
Comparison of microbial communities in three different mine drainages and their bioleaching efficien
Effects of samarium dopant on photocatalytic activity of TiO2 nanocrystallite for methylene blue deg
Simulated small-scale pilot plant heap leaching of low-grade oxide zinc ore with integrated selectiv
Hydrothermal synthesis and electrochemical properties of alpha-manganese sulfide submicrocrystals as
Expression, purification and characterization of the sulfite reductase hemo-subunit, SiR-HP, from Ac
Optimization of separation processing of copper and iron of dump bioleaching solution by Lix 984N in
Glu43 is an essential residue for coordinating the [Fe2S2] cluster of IscR from Acidithiobacillus fe
In vitro assembly of [Fe4S4] cluster in high potential iron-sulfur protein from Acidithiobacillus fe
Expression, purification and characterization of a high potential iron-sulfur protein from Acidithio
Bioleaching of sphalerite by Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans cultur
期刊信息
位置：