制作了一种新型绿色磷光有机电致发光二极管。器件结构为ITO/HAT-CN（x nm）/MoO3（30 nm）/NPB（40 nm）/TCTA（10 nm）/CPB∶GIr1（30 nm,14%）/BCP（10 nm）/Alq3（25 nm）/LiF（1 nm）/Al（100 nm）,其中X=0,8,10,12,14,15 nm。电流密度-电压-亮度特性表明该结构有利于降低驱动电压和增加器件亮度。当HAT-CN厚度为12 nm时,器件的最高亮度可以达到32 480 cd/m2,起亮电压为3.5 V左右,发光效率为24.2cd/A。所设计的空穴型器件证明该器件结构具有很好的空穴注入和传输特性。
英文摘要：
A novel structure of green phosphorescent organic light-emitting diode was fabricated.The structure of the devices was ITO/HAT-CN（x nm）/MoO3（30 nm）/NPB（40 nm）/TCTA（10 nm）/CPB∶GIr1（30 nm,14%）/BCP（10 nm）/Alq3（25 nm）/LiF（1 nm）/Al（100 nm）,in which X was 0,8,10,12,14,15 nm,respectively.The current density-voltage-luminance（J-V-L） performance shows that this structure is beneficial to the reduction of the driving voltage and the enhancement of the luminance.It was found that the best thickness was 12 nm HAT-CN layer,the highest luminance of the device was 32 480 cd/m2 at 15 V,the turn-on voltage of this device was 3.5 V and the current efficiency was 24.2 cd/A.Hole-only device was fabricated to verify the enhancement of hole injection and transport properties of this structure.
同期刊论文项目
同项目期刊论文
Electroluminescence enhancement in blue phosphorescent organic light-emitting diodes based on differ
Aluminum/MoO3 anode thin films: An effective anode structure for high-performance flexible organic o
Properties of Phosphorescent Organic Light-Emitting Diodes with Different Doping Order on Light Emit
A New Non-Contact Method Based on Relative Spectral Intensity for Determining Junction Temperature o
Cathode Formed by Thermal Evaporation of Ba:Al Alloy and Estimations of Barrier Height in an Organic
期刊信息
位置：