中文摘要：
在AZ31表面磁控溅射单层纳米Al2O3涂层,用FESEM、TEM、XRD等分析涂层的形貌和结构,用电化学工作站和摩擦磨损实验研究了涂层的耐蚀和耐磨性能。结果表明,磁控溅射获得了界面结合良好的单层致密的纳米Al2O3陶瓷涂层,在3.5%（质量分数）NaCl溶液中腐蚀电位从-1.812V提高到了-1.298V,电流密度从2.009×10-4 A/cm2下降到了6.792×10-6 A/cm2;摩擦系数从0.21下降到了0.15,磨痕从841窄化为400μm。综上所述,磁控溅射单层纳米Al2O3涂层显著地改善了镁合金的耐腐蚀和耐磨损性能。
英文摘要：
A novel protective coating, consisting of single layer （nanocrystalline Al2O3 thin film）, was deposited on the surface of AZ31 magnesium alloy. Electrochemical system and tribological tester were performed to investigate the wear and corrosion resistance of the coated AZ31 magnesium alloy, respectively. The coating reduced its friction coefficient from 0.21 to 0.15, which consequently induced a great improvement of the magnesium alloy＇s wear resistance. Furthermore, the corrosion resistance of the AZ31 magnesium alloy with the coating was also enhanced with the corrosion current density decreasing from 2. 009 ×10- 4 A/cm^2 to 6. 792 ×10 6A/cm2 in a 3.5wt% NaCl solution.
同期刊论文项目
同项目期刊论文
Effects of yttrium addition on microstructure and mechanical properties of as-extruded AZ31 magnesiu
Effects of Sn addition on as-cast microstructure, mechanical properties and casting fluidity of ZA84
Partition of Er among the constituent phases and the yield phenomenon in a semi-continuously cast Mg
Effects of yttrium addition on microstructure and mechanical properties of extruded Mg-Zn-Y-Zr magne
Numerical and physical simulation of new SPD method combining extrusion and equal channel angular pr
Influence of stacking fault energy on formation of long period stacking ordered structures in Mg&min
Comparison of as-cast microstructures and mechanical properties for Mg-4Y-1.2Mn-0.9Sc and Mg-4Y-1.2M
Effects of minor Zr and Sr on as-cast microstructure and mechanical properties of Mg-3Ce-1.2Mn-1Zn a
Comparison about Effects of Sb, Sn and Sr on As-cast Microstructure and Mechanical Properties of AZ6
Comparison of as-cast microstructures and mechanical properties for Mg-Ce-Mn-Sc and Mg-Ce-Mn-Zn magn
Processing effects on grain refinement of AZ31 magnesium alloy treated with a commercial Al-10Sr mas
Comparison about effects of Ce, Sn and Gd additions on as-cast microstructure and mechanical propert
Effects of phase composition on the mechanical properties and damping capacities of as-extruded Mg&n
期刊信息
位置：