中文摘要：
通过光学金相（OM）,扫描电镜（SEM）,X射线衍射（XRD）等分析方法,研究不同Sn含量对Mg-6Zn-1Mn（ZM61）合金显微组织和力学性能的影响,并初步探讨Sn元素在镁合金中的存在形式和作用机理。结果表明：Sn元素在ZM61合金中主要以Mg2Sn相存在;Sn元素不仅可以改善合金的铸造性能,所形成弥散的Mg2Sn相颗粒还可以明显的细化晶粒改善组织,提高合金的力学性能,其中经440℃,2h＋90℃,24h＋180℃,8h双级时效处理的ZM61-4Sn合金具有最佳的综合力学性能,其屈服强度、抗拉强度和延伸率分别为358MPa、374MPa和4.6%;Sn的加入不会改变合金的断裂机制,但是粗大的Mg2Sn粒子会成为裂纹源,从而降低合金的塑性,所以Sn含量不宜过高,不大于4%较为合适。
英文摘要：
The microstructure and mechanical properties of the ZM61 alloy （Mg-6Zn-1Mn） with different Sn content were researched by optical microscope （OM）, scanning electron microscopy （SEM）, differential scanning calorimetry （DSC）, X-ray diffraction （XRD） and tensile tests. The existence form and acting mechanism of Sn element in ZM61 alloy and the influence of Sn content on microstructure and mechanical properties were investigated. The results show that the addition of Sn can improve the casting fluidity and the formation of the dispersed Mg 2 Sn particles can refine the MgZn phase to improve the microstructure and the mechanical properties of ZM61 alloy. The ZM61-4Sn alloy with double aging treatment has the best mechanical properties, with tensile strength of 374 MPa, yield strength of 358 MPa and elongation of 4.6%. However the addition of Sn cannot change the fracture behavior of ZM61 alloy while the coarse Mg 2 Sn phase can become crack source during fracture to decrease the plasticity. Therefore, Sn content should not be too high, no more than 4%.
同期刊论文项目
同项目期刊论文
Effects of yttrium addition on microstructure and mechanical properties of as-extruded AZ31 magnesiu
Effects of Sn addition on as-cast microstructure, mechanical properties and casting fluidity of ZA84
Partition of Er among the constituent phases and the yield phenomenon in a semi-continuously cast Mg
Effects of yttrium addition on microstructure and mechanical properties of extruded Mg-Zn-Y-Zr magne
Numerical and physical simulation of new SPD method combining extrusion and equal channel angular pr
Influence of stacking fault energy on formation of long period stacking ordered structures in Mg&min
Comparison of as-cast microstructures and mechanical properties for Mg-4Y-1.2Mn-0.9Sc and Mg-4Y-1.2M
Effects of minor Zr and Sr on as-cast microstructure and mechanical properties of Mg-3Ce-1.2Mn-1Zn a
Comparison about Effects of Sb, Sn and Sr on As-cast Microstructure and Mechanical Properties of AZ6
Comparison of as-cast microstructures and mechanical properties for Mg-Ce-Mn-Sc and Mg-Ce-Mn-Zn magn
Processing effects on grain refinement of AZ31 magnesium alloy treated with a commercial Al-10Sr mas
Comparison about effects of Ce, Sn and Gd additions on as-cast microstructure and mechanical propert
Effects of phase composition on the mechanical properties and damping capacities of as-extruded Mg&n
期刊信息
位置：