东篱科研大数据发现系统（DRDS）

位置：成果数据库 > 期刊 > 期刊详情页

Effects of little Ce addition on as-cast microstructure and creep properties of Mg-3Sn-2Ca magnesium alloy

ISSN号：1003-6326
期刊名称：《中国有色金属学报：英文版》
时间：0
分类：TG146.23[金属学及工艺—金属材料;一般工业技术—材料科学与工程;金属学及工艺—金属学] TG146.22[金属学及工艺—金属材料;一般工业技术—材料科学与工程;金属学及工艺—金属学]
作者机构：[1]Materials Science and Engineering College, Chongqing University of Technology, Chongqing 400050, China, [2]Materials Science and Engineering College, Chongqing University, Chongqing 400030, China, [3]Corrosion and Protection Center, School of Materials, Manchester University, M60 1QD, United Kingdom
相关基金：Project（50725413） supported by the National Natural Science Foundation for Distinguished Young Scholar in China; Project （2007CB613704） supported by the National Basic Research Program of China; Projects（2006AA4012-9-6 and 2007BB4400） supported by the Chongqing Science and Technology Commission of China

关键词：蠕变性能, 镁合金, 铸态组织, 铈, 微观结构变化, 相体积分数, 质量分数, 帕斯卡, magnesium alloy, Mg-3Sn-2Ca alloy, CaMgSn phase, Ce

中文摘要：

当演员组微观结构上的很少 Ce 增加的效果并且爬 Mg-3Sn-2Ca 镁合金的性质被调查。结果显示那增加 0.5%( 集体部分) 到 Mg-3Sn-2Ca 合金的 Ce 不在合金引起任何新阶段的形成。然而，在与 0.5%Ce 增加的当演员组 Mg-3Sn-2Ca 合金的一个有趣的微结构变化被观察。在把 0.5%Ce 加到 Mg-3Sn-2Ca 合金，不是 CaMgSn 的仅仅体积部分以后，在合金的阶段被减少而且在合金的 CaMgSn 阶段被精制。另外，把 0.5%Ce 加到 Mg-3Sn-2Ca 合金能也改进合金的爬抵抗的性质。在把 0.5%Ce 加到 Mg-3Sn-2Ca 合金以后，第二爬在 150 吠敨牯瑥捩污猠'T 敳畱湥 ? 楹汥? 潬楣戠獡摥漠 ? 汙? 的合金的率 ?? 搲礠敩摬挠楲整楲湯愠摮琠牨敥欠湩獤漠 ? 慨摲湥湩 ? 潭敤 ? 敷敲挠污畣慬整 ? 湡 ? 潣灭牡摥眠吗？

英文摘要：

The effects of little Ce addition on the as-cast microstructure and creep properties of Mg-3Sn-2Ca magnesium alloy were investigated. The results indicate that adding 0.5% （mass fraction） Ce to Mg-3Sn-2Ca alloy does not cause the formation of any new phase in the alloy. However, an interesting microstructural change in the as-cast Mg-3Sn-2Ca alloy added with 0.5%Ce is observed. After adding 0.5%Ce to Mg-3Sn-2Ca alloy, not only the volume fraction of CaMgSn phase in the alloy is decreased but also the CaMgSn phases in the alloy are refined. In addition, adding 0.5%Ce to Mg-3Sn-2Ca alloy can also improve the creep-resistant properties of the alloy. After adding 0.5%Ce to Mg-3Sn-2Ca alloy, the second creep rate of the alloy at 150 ℃ and 70 MPa for 100 h changes from 3.28×10^-8 to 1.81 × 10^-8 s^-1.