中文摘要：
研究了Zn与Al质量比对Mg-Zn-Al三元镁合金铸态组织和凝固行为的影响。结果表明：Zn与Al质量比小于2的实验合金主要由α-Mg＋Mg32（Al, Zn）49相组成，且随着Zn与Al质量比的增加，实验合金中第二相的数量逐渐减少，同时其分布由连续网状逐渐向断续状转变；Zn与Al质量比大于2的实验合金则主要由α-Mg＋Mg32（Al, Zn）49＋MgZn相组成，且随着Zn与Al质量比的增加，实验合金中第二相的数量逐渐增加，同时其分布由断续网状逐渐向颗粒弥散状转变；此外，Zn与Al质量比小于2的实验合金的第二相转变开始温度和峰值温度基本上高于Zn与Al质量比大于2的实验合金，从而导致第二相转变过程中不同相变的发生和第二相类型的不同。
英文摘要：
The effect of mass ratio of Zn to Al on the as-cast microstructure and solidification behaviour of Mg-Zn-Al ternary magnesium alloys was investigated. The results indicate that, when the mass ratio of Zn to Al of experimental alloys are less than 2, the alloys are composed of α-Mg and Mg32（Al, Zn）49 phases, and with increasing mass ratio of Zn to Al, the amount of the second phases in the alloys gradually decreases and the distribution of the second phases changes from continuous net to quasti-continuous net. However, when the mass ratio of Zn to Al of experimental alloys is more than 2, the alloys are composed of α-Mg, Mg32（Al, Zn）49 and MgZn phases, and with increasing mass ratio of Zn to Al, the amount of the second phases in the alloys gradually increases and the distribution of the second phases changes from quasti-continuous net to uniform particles. In addition, the onset and peak temperatures of the second phase transformation for the experimental alloys with relatively low mass ratio of Zn to Al （〈2）, are higher than those of the alloys with high mass ratio of Zn to Al （〉2）, which results in different reactions during the second phase transformation and different types of the second phases.
同期刊论文项目
同项目期刊论文
Effects of yttrium addition on microstructure and mechanical properties of as-extruded AZ31 magnesiu
Effects of Sn addition on as-cast microstructure, mechanical properties and casting fluidity of ZA84
Partition of Er among the constituent phases and the yield phenomenon in a semi-continuously cast Mg
Effects of yttrium addition on microstructure and mechanical properties of extruded Mg-Zn-Y-Zr magne
Numerical and physical simulation of new SPD method combining extrusion and equal channel angular pr
Influence of stacking fault energy on formation of long period stacking ordered structures in Mg&min
Comparison of as-cast microstructures and mechanical properties for Mg-4Y-1.2Mn-0.9Sc and Mg-4Y-1.2M
Effects of minor Zr and Sr on as-cast microstructure and mechanical properties of Mg-3Ce-1.2Mn-1Zn a
Comparison about Effects of Sb, Sn and Sr on As-cast Microstructure and Mechanical Properties of AZ6
Comparison of as-cast microstructures and mechanical properties for Mg-Ce-Mn-Sc and Mg-Ce-Mn-Zn magn
Processing effects on grain refinement of AZ31 magnesium alloy treated with a commercial Al-10Sr mas
Comparison about effects of Ce, Sn and Gd additions on as-cast microstructure and mechanical propert
Effects of phase composition on the mechanical properties and damping capacities of as-extruded Mg&n
期刊信息
位置：