比较研究了Mg-3Ce-1.2Mn-0.9Sc和Mg-3Ce-1.2Mn-1Zn镁合金的铸态组织和力学性能。结果表明：含Sc合金主要由α-Mg、Mg12Ce和Mn2Sc相组成,而含Zn合金则主要由α-Mg和Mg12Ce相组成。然而,含Sc和含Zn铸态合金中Mg12Ce相的形貌是不同的。含Sc合金中的Mg12Ce相主要呈颗粒状,而含Zn合金中的Mg12Ce相则主要呈连续和/或准连续的网状。同时,含Sc合金的晶粒较含Zn合金的相对较为细小。此外,虽然含Sc合金和Zn合金在室温和300°C下具有相似的抗拉性能,但含Sc合金在300°C和30MPa下持续100h后的抗蠕变性能较Zn合金的好。
英文摘要：
The as-cast microstructures and mechanical properties of Mg-3Ce-1.2Mn-0.9Sc and Mg-3Ce-1.2Mn-1Zn magnesium alloys were investigated and compared. The results indicate that the Sc-containing alloy mainly consists of α-Mg, Mg12Ce and Mn2Sc phases, and the Zn-containing alloy is mainly composed of α-Mg and Mg12Ce phases. The morphologies of the Mg12Ce phases in the two as-cast alloys are different. The Mg12Ce phases in the Sc- and Zn-containing alloys mainly exhibit particle-like shapes and continuous and/or quasti-continuous nets, respectively. Furthermore, the grains of the Sc-containing alloy are finer than those of the Zn-containing alloy. In addition, the Sc- and Zn-containing alloys have similar as-cast tensile properties at room temperature and 300 °C. However, the Sc-containing alloy exhibits higher creep-resistant properties at 300 °C and 30 MPa for 100 h than the Zn-containing alloy.
同期刊论文项目
同项目期刊论文
Effects of yttrium addition on microstructure and mechanical properties of as-extruded AZ31 magnesiu
Effects of Sn addition on as-cast microstructure, mechanical properties and casting fluidity of ZA84
Partition of Er among the constituent phases and the yield phenomenon in a semi-continuously cast Mg
Effects of yttrium addition on microstructure and mechanical properties of extruded Mg-Zn-Y-Zr magne
Numerical and physical simulation of new SPD method combining extrusion and equal channel angular pr
Influence of stacking fault energy on formation of long period stacking ordered structures in Mg&min
Comparison of as-cast microstructures and mechanical properties for Mg-4Y-1.2Mn-0.9Sc and Mg-4Y-1.2M
Effects of minor Zr and Sr on as-cast microstructure and mechanical properties of Mg-3Ce-1.2Mn-1Zn a
Comparison about Effects of Sb, Sn and Sr on As-cast Microstructure and Mechanical Properties of AZ6
Comparison of as-cast microstructures and mechanical properties for Mg-Ce-Mn-Sc and Mg-Ce-Mn-Zn magn
Processing effects on grain refinement of AZ31 magnesium alloy treated with a commercial Al-10Sr mas
Comparison about effects of Ce, Sn and Gd additions on as-cast microstructure and mechanical propert
Effects of phase composition on the mechanical properties and damping capacities of as-extruded Mg&n
期刊信息
位置：