中文摘要：
以Ni—Mo合金粉末为原料，利用激光熔化沉积技术制备出主要由高硬度NiMo金属间化合物和高强韧性镍基固溶体γ组成的γ／NiMo近共晶合金，分析了合金的显微组织并在室温干滑动磨损条件下测试了合金的耐磨性。结果表明，γ/NiMo近共晶合金组织细小、均匀致密；由于NiMo金属间化合物的高硬度与γ的高强韧性配合，合金在两种滑动速度时的磨损量均较低且几乎不随法向载荷的增加而变化，表现出优异的磨损载荷特性，而摩擦系数随法向载荷的增加显著降低，特别是在较高滑动速度时合金反而具有较低的磨损量和摩擦系数。合金在滑动速度0．93m／s，法向载荷196N时的磨损量仅为相同条件下淬火45^#钢磨损量的1／10。
英文摘要：
A γ/NiMo near-eutectic alloy mainly consisting of NiMo intermetallic compound and Ni-based solid solution γ was fabricated by laser melting deposition process using Ni-Mo elemental powder blends. Microstructure and room temperature dry sliding wear resistance of the alloy at different sliding speeds and test loads were studied. The alloy has a homogeneous microstructure and better wear resistance even at higher sliding speed and test load. Wear volume loss of the alloy is extremely insensitive to increasing wear test load at each sliding speed while coefficient of friction drastically decreases with the increase of both sliding speed and test load, what＇s more, higher sliding speed brings lower wear volume loss and lower coefficient of friction, which is dominantly due to the combination of high hardness of the NiMo intermetallic compound and good toughness of the Ni-based solid solution γ. Wear volume loss of the alloy is only ten percent of that of hardened 0. 45% C steel under the same testing condition of 0.93 m/s sliding speed and 196 N test load.
同期刊论文项目
同项目期刊论文
Mechanical Properties and Microstructure Characteris-tics of Laser Rapid Forming Rene88DT Superalloy
Microstructure and hot corrosion behaviors of a gamma-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal s
Hot corrosion behaviors of a Cr13Ni5Si2-based metal silicide alloy in Na2SO4+25 wt.% K2SO4 and Na2SO
Microstructure and mechanical properties of rapid directionally solidified Ni-base superalloy Rene'4
High temperature mechanical properties of a laser melting deposited TiC/TA15 titanium matrix composi
Deformation Behavior in High-Frequency Fatigue Failure of Laser Melting Deposited Ti-6Al-2Zr-Mo-V Al
Microstructure and Tribological Property of Laser Melt Deposited alpha/Fe9Cr9Si2 Metal Silicide Allo
Effect of Annealing Temperatures on Microstructure and Mechanical Properties of Laser Melting Deposi
Microstructure and mechanical properties of directional rapidly solidified Ni-base superalloy Rene95
Microstructure and electrochemical characterization of laser melt-deposited Ti2Ni3Si/NiTi intermetal
Corrosion behaviors of a gamma-toughened Cr13Ni5Si2/Cr3Ni5Si2 multi-phase ternary metal silicide all
CORROSION BEHAVIORS OF Ni BASE SOLID SOLUTION-TOUGHENED Cr13Ni5Si2 ALLOY IN Cl- CONTAINING SOLUTIONS
Microstructure and dry sliding wear resistance of laser clad TiC reinforced Ti-Ni-Si intermetallic c
Microstructural characterization and dry sliding wear resistance of MoO2-strengthened gamma/NiMo all
Microstructure and tensile properties of laser melting deposited TiC/TA15 titanium matrix composites
Solidification microstructure and mechanical properties of corrosion-resistant ultrahigh strength st
Influence of Ni content on the microstructure and dry sliding wear properties of Cr13Ni5Si2/gamma in
Microstructure and wear resistance of laser melted Ti5Si3-TiCo-Ti2Co multiphase intermetallic alloys
期刊信息
位置：