中文摘要：
采用化学气相渗透（CVI）结合溶液浸溃法制备3D-C／SiC-（W—C）多元基复合材料，利用XRD、SEM技术对材料烧蚀前后的物相组成及微观结构进行表征，并讨论了复合材料的烧蚀性能。结果表明，3D-C／SiC-（W—C）复合材料的主要成分为WC、W、SiC和C，而烧蚀表面的主要成分为WO3、W和SiC。W—C不仅渗入纤维束间，还渗入到纤维束内。制得的C／SiC-（W-C）复合材料密度为3．3g／cm^3，开气孔率为11％，其线烧蚀率和质量烧蚀率分别为4．3×10^-2mm／s和7．2×10^-3g／s。
英文摘要：
A 3D C/SiC-（W-C） composite was prepared by combining chemical vapor infiltration （CVI） technology with solution impregnation method. The phase composition and microstructure of the composite before and after ablation were investigated by XRD, and SEM, respectively. The ablation properties of as-prepared C/SiC-（W-C） composite were studied. The XRD results show that the main phases of the as-prepared composite are WC, W, SiC and C while those of the ablated surface are WO3, W and SiC. SEM analysis implies that not only inter-bundle pores but also intra-bundle pores are filled by W-C. The as-prepared C/SiC-（W-C） composite attains a density of 3.3 g/cm^3 with the apparent porosity of 11%. Its linear and mass ablation rates are 4.3×10^-2mm/s and7.2×10^-3g/s, respectively.
同期刊论文项目
同项目期刊论文
Stress-Oxidationbehavior of a carbon/silicon carbide composite in a high temperature combustion envi
Tensile behavior and microstructural evolution of a carbon/silicon carbide composite in simulated re
Effect of temperature gradients and stress levels on damage of C/SiC composites in oxidizing atmosph
Experimental simulation of the space re-entry environment for a carbon/silicon carbide composite and
期刊信息
位置：