中文摘要：
用ZrB2微粉对2D C/SiC基体进行改性,研究了化学气相渗透结合浆料浸渍及先驱体浸渍裂解工艺制备2DC/SiC-ZrB2复合材料在氧-乙炔焰和1800℃甲烷风洞环境中的烧蚀行为。结果表明：在氧-乙炔环境中,2D C/SiC-ZrB2的线烧蚀率和质量烧蚀率分别为6.1×10-2mm/s和1.0×10-2g/s,相对2D C/SiC复合材料而言,ZrB2微粉并没有提高C/SiC复合材料的抗烧蚀性能。在1800℃甲烷风洞环境中,涂层致密度起主要作用,涂层致密度相同时,复合材料的开气孔率越大,质量烧蚀率越大,ZrB2微粉的渗入对C/SiC复合材料的烧蚀性能影响不大。
英文摘要：
2D C/SiC-ZrB2 composite was fabricated by combining chemical vapor infiltration,ZrB2 slurry infiltration and polymer infiltration and pyrolysis method.The ablation properties of the composite under oxyacetylene flame and 1800℃ methane combustion wind tunnel were studied.The results show that under the oxyacetylene flame environment,the linear ablation rate and the mass ablation rate of the 2D C/SiC-ZrB2 are 6.1×10-2mm/s and 1.0×10-2g/s respectively.The anti-ablation performance is improved by infiltrated ZrB2 particles into C/SiC matrix.Under the 1800℃methane combustion wind tunnel,the coating density plays a major role on the ablation behavior.At the same coating density,the mass ablation rate increases with the open porosity of the composites.The addition of ZrB2 to C/SiC has little effect on the anti-ablation performance.
同期刊论文项目
同项目期刊论文
Nondestructive evaluation and mechanical characterization of a defect-embedded ceramic matrix compos
Behavior of two-dimensional C/SiC composites subjected to thermal cycling in controlled environments
The Acoustic Emission Characteristics of Silicon Carbide Firber Reinforced composite Under Tensile L
Acoustic Emission Research on Thermal Shock Behaviors of Three-Dimensional C/SiC Composites in Diffe
Damage analysis of 2D C/SiC composites subjected to thermal cycling in oxidizing environments by mec
Thermal expansion behavior of carbon fiber reinforced chemical-vapor-infiltrated silicon carbide com
Thermal cycling response behavior of ceramic matrix composites under load and displacement constrain
Damage mechanisms of C/SiC composites subjected to constant load and thermal cycling in oxidizing at
Effect of shrinkage constraint on damage of C/SiC composites during thermal cycles in oxidising atmo
Numerical Simulation of Effect of Methyltrichlorosilane Flux on Isothermal Chemical Vapor Infiltrati
Thermal cycling damage mechanisms of C/SiC composites in displacement constraint and oxidizing atmos
Comparative Modeling of Gas Transport in Isothermal Chemical Vapor Infiltration Process of C/SiC Com
Modeling the effects of thermal and mechanical load cycling on a C/SiC composite in oxygen/argon mix
Relationship of damage evolution of ceramic matrix composites between static and dynamic oxidizing g
Residual strength prediction of SiC/SiC composite exposed to service environments with factor analys
Monotonic tensile behavior analysis of three-dimentional needle-punched Wover C/SiC Composites by Ac
Life Prediction of 3D woven C/SiC Composites at High Temperatures with Low Frequency Cyclic Stresses
Experimental research on failure mechanism of a CVI-fabricated ceramic matrix composite under compre
Tension-tension fatigue damage characteristics of a 3D SiC/SiC composite in H2O-O2-Ar environment at
Oxidation protective multilayer CVD SiC coatings modified by a graphitic B-C interlayer for 3D C/SiC
Characterization of tensile behavior of a two-dimensional woven carbon/silicon carbide composite fab
Stress-Oxidationbehavior of a carbon/silicon carbide composite in a high temperature combustion envi
Tensile behavior and microstructural evolution of a carbon/silicon carbide composite in simulated re
Effect of temperature gradients and stress levels on damage of C/SiC composites in oxidizing atmosph
Experimental simulation of the space re-entry environment for a carbon/silicon carbide composite and
期刊信息
位置：