中文摘要：
采用全方位离子注入和沉积（Plasma Immersion Ion Implamation and Deposition，PⅢ＆D），在SiC涂层表面形成注入沉积改性层（改性元素A1和Si），观察了离子注入和沉积对涂层表面裂纹的封填情况，分析了离子注入和沉积后涂层表面的相组成，考核了离子注入和沉积对SiC-C／SiC材料抗氧化性能的影响。实验结果表明：注入AI再注入沉积Si改性后显著降低复合材料在1300℃空气中的氧化质量损失，提高了复合材料的抗氧化能力，边注入边沉积Al和同时全方位沉积AI和Si改性对复合材料抗氧化性能改善作用较小，边注入边沉积Si改性改善复合材料抗氧化性能的作用最小。
英文摘要：
CVD SiC coating is implanted with AI and Si by PⅢ＆D respectively. The effect of ion implantation on sealing cracks of SiC coating is observed by SEM and the phase presented in the coating surface are analyzed by XRD. Oxidation is conducted in simulated air at 1300℃ for 15 hours to evaluate the effect of ion implantation on oxidation resistance of the coating. Tests indicate that after oxidation in air at 130℃ the weight loss of the MEVVA AI/PIID Si modified composite decreases, the oxidation resistance property of the coposite is modified, the oxidation resistance of the PⅢ＆D AI and PIID AI ＆Si composite is less modified, and the oxidation resistance of the PⅢ＆D Si composite is least modified.
同期刊论文项目
同项目期刊论文
Nondestructive evaluation and mechanical characterization of a defect-embedded ceramic matrix compos
Behavior of two-dimensional C/SiC composites subjected to thermal cycling in controlled environments
The Acoustic Emission Characteristics of Silicon Carbide Firber Reinforced composite Under Tensile L
Acoustic Emission Research on Thermal Shock Behaviors of Three-Dimensional C/SiC Composites in Diffe
Damage analysis of 2D C/SiC composites subjected to thermal cycling in oxidizing environments by mec
Thermal expansion behavior of carbon fiber reinforced chemical-vapor-infiltrated silicon carbide com
Thermal cycling response behavior of ceramic matrix composites under load and displacement constrain
Damage mechanisms of C/SiC composites subjected to constant load and thermal cycling in oxidizing at
Effect of shrinkage constraint on damage of C/SiC composites during thermal cycles in oxidising atmo
Numerical Simulation of Effect of Methyltrichlorosilane Flux on Isothermal Chemical Vapor Infiltrati
Thermal cycling damage mechanisms of C/SiC composites in displacement constraint and oxidizing atmos
Comparative Modeling of Gas Transport in Isothermal Chemical Vapor Infiltration Process of C/SiC Com
Modeling the effects of thermal and mechanical load cycling on a C/SiC composite in oxygen/argon mix
Relationship of damage evolution of ceramic matrix composites between static and dynamic oxidizing g
Residual strength prediction of SiC/SiC composite exposed to service environments with factor analys
Monotonic tensile behavior analysis of three-dimentional needle-punched Wover C/SiC Composites by Ac
Life Prediction of 3D woven C/SiC Composites at High Temperatures with Low Frequency Cyclic Stresses
Experimental research on failure mechanism of a CVI-fabricated ceramic matrix composite under compre
Tension-tension fatigue damage characteristics of a 3D SiC/SiC composite in H2O-O2-Ar environment at
Oxidation protective multilayer CVD SiC coatings modified by a graphitic B-C interlayer for 3D C/SiC
Characterization of tensile behavior of a two-dimensional woven carbon/silicon carbide composite fab
Stress-Oxidationbehavior of a carbon/silicon carbide composite in a high temperature combustion envi
Tensile behavior and microstructural evolution of a carbon/silicon carbide composite in simulated re
Effect of temperature gradients and stress levels on damage of C/SiC composites in oxidizing atmosph
Experimental simulation of the space re-entry environment for a carbon/silicon carbide composite and
期刊信息
位置：