中文摘要：
用静电纺丝技术成功制备出大量的TiO2@SiO2亚微米同轴电缆．用TGA—DTA，XRD，SEM，TEM，EDS，FTIR分析技术对样品结构和组成进行了系统的表征．结果表明，得到的产物为TiO2@SiO2亚微米级同轴电缆，以无定型SiO2为壳层，晶态TiO2为芯层，电缆平均直径450nm，壳层厚度90nm，电缆长度〉300gm，同时在样品中发现个别纤维呈现管状结构，对其形成机理进行了讨论．
英文摘要：
Highly-yielded TiO2@SiO2 submicron-scaled coaxial cables have been successfully synthesized via a static electricity spinning technology. The microstructures and components of the samples were studied by TGA-DTA, XRD, SEM, TEM, EDS and FTIR techniques. The as-prepared sub-micro coaxial cables with a mean diameter of 450 nm and shell thickness of 90 nm had a crystalline TiO2 core and an amorphous shell of SiO2. The length of the TiO2@SiO2 cable was longer than 300 μm. Some submicron tubes were also found in the samples, and their formation mechanisms were also discussed in detail.