中文摘要：
采用超声喷雾热分解法在石英衬底上以醋酸锌水溶液为前驱体,以硝酸银水溶液为Ag掺杂源生长了Ag掺杂ZnO（ZnO：Ag）薄膜.研究了衬底温度对所得ZnO：Ag薄膜的晶体结构、电学和光学性质的影响规律.所得ZnO：Ag薄膜结构良好,在室温光致发光谱中检测到很强的近带边紫外发光峰,透射光谱中观测到非常陡峭的紫外吸收截止边和较高的可见光区透过率,表明薄膜具有较高的晶体质量与较好的光学特性.霍尔效应测试表明,在500℃下获得了p型导电的ZnO：Ag薄膜,载流子浓度为5.30×10^15cm^-3,迁移率为6.61cm2·V^-1s^-1.
英文摘要：
Ag doped ZnO films（ZnO：Ag） were deposited on quartz glass substrates by ultrasonic spray pyrolysis technology.Zn（CH_3COO）_2 and Ag（NO_3）_3 aqueous solution were used as the sources of Zn and Ag,respectively.The effect of substrate temperature on structural,electrical and optical properties of ZnO：Ag films were studied using X-ray diffraction,Hall effect measurement,photoluminescence spectra,and transmittance spectra measurement.All the measurements were performed at room temperature.It is found that the electrical and optical properties of the obtained ZnO：Ag thin films change dramatically due to Ag doping.The Ag doped p-type ZnO films with hole carrier concentration of 5.295×1015？cm-3 and Hall mobility of 6.61？cm2·V-1s-1 at room temperature have been successfully obtained at optimal conditions.In photoluminescence measurements,a strong ultraviolet emission centered at 379？nm and a relatively weak green emission band were observed,and in transmittance measurements,a high transmittance of ～70% in the visible region and a sharp absorption edge at 375？nm were observed for all samples.
同期刊论文项目
同项目期刊论文
Annealing effects on electrical and optical properties of ZnO films deposited on GaAs by metal organ
Room temperature electroluminescence from the ZnO homojunction grown on an n(+)-Si substrate by meta
p-type ZnO thin films prepared by metal organic chemical vapor deposition using metal organic dopant
Effect of the magnesium composition on the properties of MgxZn1-xO-based homojunction light-emitting
Enhanced p-type ZnO films through nitrogen and argentum codoping grown by ultrasonic spray pyrolysis
Realization of ultraviolet electroluminescence from ZnO homojunction with n-ZnO /p-ZnO:As/GaAs struc
Room temperature defect related electroluminescence from ZnO homojunctions grown by ultrasonic spray
Visual-infrared electroluminescence emission from ZnO/GaAs heterojunctions grown by metal-organic ch
Electroluminescence from n-ZnO/p-ZnO:Sb homojunction light emitting diode on sapphire substrate with
Optical and electronic propertyes of ZnO:P/n+-Si heterostructures fabricated by metalorganic chemica
Room temperature electroluminescence from the n-ZnMgO/ZnO/p-ZnMgO heterojunction device grown by ult
Optical and electronic properties of ZnO : P/n(+)-Si heterostructures fabricated by metalorganic che
p-Type Sb-Doped ZnO Thin Films Prepared by Metallorganic Chemical Vapor Deposition Using Metallorgan
Electroluminescence from n-ZnO/p-ZnO : Sb homojunction light emitting diode on sapphire substrate wi
Photoluminescence and X-Ray Photoelectron Spectroscopy of p-Type Phosphorus-Doped ZnO Films Prepared
Photoluminescence investigation of ZnO:P nanoneedle arrays on InP substrate by pulsed laser depositi
Photoluminescence study of novel phosphorus-doped ZnO nanotetrapods synthesized by chemical vapour d
Effect of Different Substrate Temperature on Phosphorus-Doped ZnO Thin Films Prepared by PLD on Sapp
Room temperature electroluminescence from ZnO/Si heterojunction devices grown by metal-organic chemi
Realization of controllable etching for ZnO film by NH4Cl aqueous solution and its influence on opti
Effect of anneal on the properties of MgxZn1-xO thin films deposited by metal-organic chemical vapor
Synthesis and defect-related emission of ZnO based light emitting device with homo- and heterostruct
Synthesis and temperature dependent photoluminescence of Zn(1-x)Mg(x)Ofilms grown by ultrasonic spra
Realization of ultraviolet electroluminescence from ZnO homojunction with n-ZnO/p-ZnO:As/GaAs struct
位置：