中文摘要：
依据JEDEC标准采用板级跌落实验研究晶圆级芯片尺寸封装Sn-3.0Ag-0.5Cu焊点的跌落失效模式。发现存在六种失效模式,即发生在印刷电路板（PCB）侧的短FR-4裂纹和完全FR-4裂纹,以及发生在芯片侧的再布线层（RDL）与Cu凸点化层开裂、RDL断裂、体钎料裂纹及体钎料与界面金属间化合物（IMC）混合裂纹。对于最外侧的焊点,由于PCB变形量较大且FR-4介质层强度较低,易于形成完全FR-4裂纹,其可吸收较大的跌落冲击能量,从而避免了其它失效模式的发生。对于内侧的焊点,先形成的短FR-4裂纹对跌落冲击能量的吸收有限,导致在芯片侧发生失效。
英文摘要：
To reveal the drop failure modes of the wafer level chip scale packages （WLCSPs） with Sn-3.0Ag-0.5Cu solder joints, board level drop tests were performed according to the JEDEC standard. Six failure modes were identified, i.e., short FR-4 cracks and complete FR-4 cracks at the printing circuit board （PCB） side, split between redistribution layer （RDL） and Cu under bump metallization （UBM）, RDL fracture, bulk cracks and partial bulk and intermetallic compound （IMC） cracks at the chip side. For the outmost solder joints, complete FR-4 cracks tended to occur, due to large deformation of PCB and low strength of FR-4 dielectric layer. The formation of complete FR-4 cracks largely absorbed the impact energy, resulting in the absence of other failure modes. For the inner solder joints, the absorption of impact energy by the short FR-4 cracks was limited, resulting in other failure modes at the chip side.
同期刊论文项目
同项目期刊论文
A synchrotron radiation real-time in situ imaging study on the reverse polarity effect in Cu/Sn-9Zn/
EFFECT OF ELECTROLESS Ni-P CONSUMPTION ON THE FAILURE MECHANISM OF SOLDER JOINTS DURING ELECTROMIGRA
Cu-Ni cross-solder interaction in Cu/Sn-58Bi/Ni interconnect undergoing liquid-solid electromigratio
Growth kinetics of Cu6Sn5 intermetallic compound at liquid-solid interfaces in Cu/Sn/Cu interconnect
In situ study on reverse polarity effect in Cu/Sn-9Zn/Ni interconnect undergoing liquid-solid electr
Effect of Cu-Ni cross-solder interaction on liquid-solid interfacial reaction in Cu/Sn/Ni solder joi
Reverse polarity effect and cross-solder interaction in Cu/Sn-9Zn/Ni interconnect during liquid-soli
Abnormal Diffusion Behavior of Zn in Cu/Sn-9 wt.%Zn/Cu Interconnects During Liquid-Solid Electromigr
Influence of Rare Earth Ce Addition on the Microstructure, Properties and Soldering Reaction of Pure
Synchrotron radiation real-time in situ study on dissolution and precipitation of Ag3Sn plates in su
Microstructure and interfacial reaction of Sn-Zn-x(Al,Ag) near-eutectic solders on Al and Cu substra
Liquid-state and solid-state interfacial reactions between Sn-Ag-Cu-Fe composite solders and Cu subs
In situ study of the real-time growth behavior of Cu6Sn5 at the Sn/Cu interface during the soldering
Effect of thermomigration on the growth kinetics of Cu6Sn5 at liquid-solid interfaces in Cu/Sn/Cu so
Stress relaxation and failure behavior of Sn-3.0Ag-0.5Cu flip-chip solder bumps undergoing electromi
Effect of Electromigration on the Type of Drop Failureof Sn3.0Ag0.5Cu Solder Joints in PBGA Packages
Effects of rare earth Ce addition on the microstructure, wettability and interfacial reactions of eu
Size effect on tensile properties of Cu/Sn–9Zn/Cu solder interconnects under aging and current stres
In situ study on the effect of thermomigration on intermetallic compounds growth in liquid-solid int
Solder Volume Effect on Interfacial Reaction between Sn-3.0Ag-0.5Cu Solder Balls and Cu Substrates -
Solder Size Effect on Early Stage Interfacial Intermetallic Compound Evolution in Wetting Reaction o
期刊信息
位置：