中文摘要：
用高分辨率X-射线光电子能谱（XPS）研究了热极化和电晕极化的PVDF薄膜的成分和结构的变化。结果表明：PVDF薄膜的热极化和电晕极化反应过程和机理不同。在热极化过程中.高温强电场作用使PVDF薄膜产生了少量的F^-自由基,继而产生HF,形成了新C=C键：怛是,在电晕极化过程中荷能粒子使PVDF产生了H^＋自由基。热极化PVDF薄膜的剩余极化值约为3.5μC/cm^2,电晕极化PVDF薄膜的剩余极化值约为3.0μC/cm^2。
英文摘要：
The component and structure of thermally poled and corona charged PVDF films were investigated by the aid of high-resolution X-ray photoelectron spectroscopy（XPS）.The results of XPS and ferroelectric properties show that the reaction and mechanism of thermally poling and corona charging for PVDF films was distinct.With the effect of high electric field at high temperature in thermally poling, a new carbon couple bond was created through the action of HF which was produced by F^- radicals. However,the H~＋ radicals engendered due to bombardment of particles during corona charging.And the remanent polarization of thermally poled PVDF film is about 3.5μC/cm^2,while that of corona charged PVDF film is about 3.0μC/cm^2.
同期刊论文项目
同项目期刊论文
Study?on?temperature?characteristics?of?organic?light-emitting?diodes?based?on?tris-(8-hydroxylquino
Efficient Blue Organic Light-emitting Diodes with Simple Structure Based on N,N'-bis(1-naphthy)-N,N'
Efficient white organic light-emitting devices using a thin 4,4'-bis(2,2'-diphenylvinyl)-1,1'-diphen
Self-assembly of Tio2/polypyrrole nanocomposite ultrathin films and application for an NH3 gas senso
Luminescent Enhancement of Heterostructure Organic Light-Emitting Devices Based on Aluminum Quinolin
Influences of fluorine auxochrome in fluorene molecular electroluminescent material on optoelectroni
Efficient bright white organic light-emitting diode based on non-doped ultrathin 5,6,11,12-tetraphen
Fabrication and nonlinear optical properties of polymeric thin films doped with a novel tricyanofura
Low roll-off power efficiency of organic light-emitting diodes consisted of nondoped ultrathin phosp
X-ray photoelectron spectroscopy characterization of the interface between Ag electrode and PVDF fil
Spectral Characteristics of White Organic Light-emitting Diodes Based on Novel Phosphorescent Sensit
Color-tunable organic light-emitting devices using a thin N,N prime -bis-(1-naphthyl)-N,N prime -dip
Electron irradiation effects on the properties of heavily phosphorus-doped a-Si ,H films prepared fr
Efficeng small molecular and polymer organic devices using bis[2-(4-tert-butylpheny)benzothiazolato-
Study on tempeature characteristica of organic light-emitting diodes based on tris-(8-hydrocylquinol
Influence of PVK: NPB hole transporting layer on the charcateristics of organic light-emitting devic
Conducting polymericnanoparticles synthesized in reverse micelles and their gas sensitivity based on
Low energy emission bands in a small molecular fluorene derivative for organic light-emitting dioeds
Fiexible organic light-emitting diodes with improved performance by insertion of an UV-sensitive lay
期刊信息
位置：