中文摘要：
通过LaZnSbO在La3＋的位置用A=Ca^2＋,Sr^2＋,Ba^2＋进行变价替换引入P型载流子,使用Mn^2＋替换Zn^2＋引入自旋,可使ZrCuSiAs结构单相（La,A）（Zn,Mn）SbO（A=Ca,Sr,Ba）同时兼具半导体和铁磁性能,居里温度可达到40K。居里温度以下呈现类似玻璃磁性的磁性特征,（La0.95Ca0.05）（Zn0.9Mn0.1）SbO的翻转时间（τ＊）和动态临界指数（zγ）分别为：τ＊=2.64×10^-7s,zγ=1.91。
英文摘要：
This thesis shows the process in which charge is induced by substitution of A=Ca^2＋, Sr^2＋, Ba^2＋for La^3＋, while spin is induced by partial substitution of Mn^2＋for Zn2＋within the parent compound LaZnSbO. The re-sults indicate that the single phase ZrCuSiAs-type tetragonal crystal structure is preserved in （La,A）（Zn,Mn）SbO （A=Ca,Sr,Ba）. The system remains semiconducting, doping with A and Mn results in ferromagnetic order with Tc 40 K. A spin-glass like state is found in （La0.95Ca0.05）（Zn0.9Mn0.1）SbO below Cure temperature which flipping time and dynamical critical are 2.64×10^-7s and 1.91 respectively.